Carpenter Pyrowear® 675 Stainless Steel, Tempered 316°C, Longitudinal Properties

Category	Metal , Ferrous Metal , Stainless Steel
Manufacturer	Carpenter Technology Corporation (Cartech)
Trade Name	Pyrowear®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Carpenter Pyrowear® 675 Stainless Steel, Tempered 316°C, Longitudinal Properties.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Data provided by Carpenter Technology Corporation.This is a carburizing, corrosion resistant steel designed to provide a case hardness in excess of HRC 60 combined with a tough, ductile core. The corrosion resistance of carburized Pyrowear® 675 stainless is similar to that of Type 440C stainless, while the core toughness is similar to that of AISI 9310. In addition, the alloy provides excellent hot hardness capability. This alloy has been used in bearing and gear type applications.Pyrowear® is a registered trademark of Carpenter Technology Corporation.

Physical Properties	Metric	English	Comments
Density	7.756 g/cc	0.2802 lb/in³

Mechanical Properties	Metric	English	Comments
Hardness, Brinell	379	379	Estimated from Rockwell C for 3000 kg load, 10 mm ball Brinell measurement.
Hardness, Knoop	414	414	Estimated from Rockwell C
Hardness, Rockwell C	41	41
Hardness, Vickers	396	396	Estimated from Rockwell C
Tensile Strength, Ultimate	1276 MPa	185100 psi
Tensile Strength, Yield	986 MPa @Strain 0.200 %	143000 psi @Strain 0.200 %
Elongation at Break	20 %	20 %	In 4D
Reduction of Area	73 %	73 %
Modulus of Elasticity	204 GPa	29600 ksi
Fracture Toughness	165 MPa-m½	150 ksi-in½	K(Q)

Thermal Properties	Metric	English
CTE, linear	10.01 µm/m-°C @Temperature 25.0 - 93.0 °C	5.561 µin/in-°F @Temperature 77.0 - 199 °F
	10.62 µm/m-°C @Temperature 25.0 - 260 °C	5.900 µin/in-°F @Temperature 77.0 - 500 °F
	11.56 µm/m-°C @Temperature 25.0 - 538 °C	6.422 µin/in-°F @Temperature 77.0 - 1000 °F

Component Elements Properties	Metric	English	Comments
Carbon, C	0.070 %	0.070 %
Chromium, Cr	13 %	13 %
Cobalt, Co	5.4 %	5.4 %
Iron, Fe	76 %	76 %	as remainder
Manganese, Mn	0.65 %	0.65 %
Molybdenum, Mo	1.8 %	1.8 %
Nickel, Ni	2.6 %	2.6 %
Phosphorous, P	<= 0.040 %	<= 0.040 %
Vanadium, V	0.60 %	0.60 %