A. Schulman POLYFLAM™ RPP 1174 Talc Filled, Homopolymer Polypropylene

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Flame Retardant
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF A. Schulman POLYFLAM™ RPP 1174 Talc Filled, Homopolymer Polypropylene.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
DescriptionPolyflam® RPP 1174 is a high performance talc filled homopolymer polypropylene product with UL V0 flammability and 105°C temperature index at 0.81 mm. RPP 1174 is non-dripping and has excellent dimensional stability.Information provided by A. Schulman.
Physical Properties Metric English Comments
Specific Gravity 1.38 g/cc
1.38 g/cc
ASTM D792
Linear Mold Shrinkage 0.0090 - 0.012 cm/cm
0.0090 - 0.012 in/in
ASTM D955
Melt Flow 8.0 g/10 min
8.0 g/10 min
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength, Yield 22.0 MPa
3190 psi
ASTM D638
Elongation at Break 45 %
45 %
ASTM D638
Flexural Modulus 2.00 GPa
290 ksi
ASTM D790
Izod Impact, Notched 0.270 J/cm
0.506 ft-lb/in
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 116 °C
241 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 69.0 °C
156 °F
ASTM D648
UL RTI, Electrical 105 °C
221 °F
0.030 inch sample
Flammability, UL94 V-0

@Thickness 0.810 mm
V-0

@Thickness 0.0319 in
V-0

@Thickness 1.57 mm
V-0

@Thickness 0.0618 in
V-0

@Thickness 3.05 mm
V-0

@Thickness 0.120 in