Lanxess DurethanÂ® T 40 000000 Partially aromatic polyamide

Category	Polymer , Thermoplastic , Nylon , Nylon, Aromatic
Manufacturer	Lanxess
Trade Name	Durethan®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Lanxess DurethanÂ® T 40 000000 Partially aromatic polyamide.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Partially aromatic polyamide, injection molding and extrusion grade, transparent in all wall thicknesses, isotropic shrinkage, mechanical and electrical properties largely unaffected by conditioning state, meets the ISO 10993-1 biocompatibility tests

Physical Properties	Metric	English	Comments
Density	1.18 g/cc	0.0426 lb/inÂ³	ISO 1183
Water Absorption	6.0 %	6.0 %	Test Sim. to ISO 62
Moisture Absorption at Equilibrium	2.0 %	2.0 %	23Â°C/50% R.H.; Test Sim. to ISO 62
Viscosity Test	107 cmÂ³/g	107 cmÂ³/g	Viscosity number; ISO 307, 1157, 1628

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	90.0 MPa	13100 psi	Conditioned; ISO 527-1/-2
	110 MPa	16000 psi	ISO 527-1/-2
Elongation at Yield	5.0 %	5.0 %	Conditioned; ISO 527-1/-2
	6.0 %	6.0 %	ISO 527-1/-2
Tensile Modulus	3.00 GPa	435 ksi	ISO 527-1/-2
	3.30 GPa	479 ksi	Conditioned; ISO 527-1/-2
Charpy Impact Unnotched	NB @Temperature -30.0 Â°C	NB @Temperature -22.0 Â°F	ISO 179/1eU
	NB @Temperature -30.0 Â°C	NB @Temperature -22.0 Â°F	Conditioned; ISO 179/1eU
	NB @Temperature 23.0 Â°C	NB @Temperature 73.4 Â°F	ISO 179/1eU
	NB @Temperature 23.0 Â°C	NB @Temperature 73.4 Â°F	Conditioned; ISO 179/1eU
Charpy Impact, Notched	<= 1.00 J/cmÂ² @Temperature -30.0 Â°C	<= 4.76 ft-lb/inÂ² @Temperature -22.0 Â°F	ISO 179/1eA
	<= 1.00 J/cmÂ² @Temperature -30.0 Â°C	<= 4.76 ft-lb/inÂ² @Temperature -22.0 Â°F	Conditioned; ISO 179/1eA
	<= 1.00 J/cmÂ² @Temperature 23.0 Â°C	<= 4.76 ft-lb/inÂ² @Temperature 73.4 Â°F	ISO 179/1eA
	<= 1.00 J/cmÂ² @Temperature 23.0 Â°C	<= 4.76 ft-lb/inÂ² @Temperature 73.4 Â°F	Conditioned; ISO 179/1eA

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	70.0 Âµm/m-Â°C	38.9 Âµin/in-Â°F	ISO 11359-1/-2
CTE, linear, Transverse to Flow	80.0 Âµm/m-Â°C	44.4 Âµin/in-Â°F	ISO 11359-1/-2
Deflection Temperature at 0.46 MPa (66 psi)	115 Â°C	239 Â°F	ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)	105 Â°C	221 Â°F	ISO 75-1/-2
Vicat Softening Point	125 Â°C	257 Â°F	50Â°C/h 50N; ISO 306
Flammability, UL94	V-2 @Thickness 1.60 mm	V-2 @Thickness 0.0630 in	IEC 60695-11-10
	V-2 @Thickness 3.20 mm	V-2 @Thickness 0.126 in	IEC 60695-11-10

Optical Properties	Metric	English	Comments
Transmission, Visible	90 %	90 %	transparent; thickness not quantified

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+15 ohm-cm	1.00e+15 ohm-cm	IEC 60093
	1.00e+15 ohm-cm	1.00e+15 ohm-cm	Conditioned; IEC 60093
Surface Resistance	1.00e+15 ohm	1.00e+15 ohm	IEC 60093
Dielectric Constant	3.8 @Frequency 1.00e+6 Hz	3.8 @Frequency 1.00e+6 Hz	IEC 60250
	4.0 @Frequency 1.00e+6 Hz	4.0 @Frequency 1.00e+6 Hz	Conditioned; IEC 60250
	4.3 @Frequency 100 Hz	4.3 @Frequency 100 Hz	IEC 60250
	4.6 @Frequency 100 Hz	4.6 @Frequency 100 Hz	Conditioned; IEC 60250
Dielectric Strength	25.0 kV/mm	635 kV/in	IEC 60243-1
	28.0 kV/mm	711 kV/in	Conditioned; IEC 60243-1
Dissipation Factor	0.040 @Frequency 100 Hz	0.040 @Frequency 100 Hz	IEC 60250
	0.048 @Frequency 100 Hz	0.048 @Frequency 100 Hz	Conditioned; IEC 60250
	0.090 @Frequency 1.00e+6 Hz	0.090 @Frequency 1.00e+6 Hz	IEC 60250
	0.11 @Frequency 1.00e+6 Hz	0.11 @Frequency 1.00e+6 Hz	Conditioned; IEC 60250
Comparative Tracking Index	600 V	600 V	IEC 60112

Descriptive Properties	Value	Comments
Form	Pellets
ISO Shortname	ISO 1874-PA 6I,MT,12-030
Processing	Injection molding
	Other extrusion
Region	Asia Pacific
	Europe
	Near East/Africa
	North America
	South and Central America