- Lanxess Durethan® DP AKV 30 FN00 000000 Nylon 66, 30% Glass Fiber
Lanxess Durethan® DP AKV 30 FN00 000000 Nylon 66, 30% Glass Fiber
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled , Nylon 66, Glass Fiber Filled, Flame Retardant |
| Manufacturer | Lanxess |
| Trade Name | Durethan® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Durethan® DP AKV 30 FN00 000000 Nylon 66, 30% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PA 66, injection molding 30% glass fibers, UL 94 V-0 at 0.4 mm, max. temperature in glow wire test: 960 °C at 0,75 mm, free from halogen and red phosphorous
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.417 g/cc | 0.05119 lb/in³ | ISO 1183 |
| Viscosity Test | 135 cm³/g | 135 cm³/g | Viscosity number; ISO 307, 1157, 1628 |
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm | 0.0020 in/in | ISO 294-4, 2577 |
| Linear Mold Shrinkage, Transverse | 0.0070 cm/cm | 0.0070 in/in | ISO 294-4, 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 85.0 MPa | 12300 psi | Conditioned; ISO 527-1/-2 |
| 135 MPa | 19600 psi | ISO 527-1/-2 | |
| Elongation at Break | 2.8 % | 2.8 % | ISO 527-1/-2 |
| 5.4 % | 5.4 % | Conditioned; ISO 527-1/-2 | |
| Tensile Modulus | 6.50 GPa | 943 ksi | Conditioned; ISO 527-1/-2 |
| 10.5 GPa | 1520 ksi | ISO 527-1/-2 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 260 °C | 500 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | >= 250 °C | >= 482 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 224 °C | 435 °F | ISO 75-1/-2 |
| Flammability, UL94 | V-0 | V-0 | IEC 60695-11-10 |
| V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
IEC 60695-11-10 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 5.00e+12 ohm-cm | 5.00e+12 ohm-cm | Conditioned; IEC 60093 |
| 5.00e+15 ohm-cm | 5.00e+15 ohm-cm | IEC 60093 | |
| Surface Resistance | 4.00e+14 ohm | 4.00e+14 ohm | IEC 60093 |
| Dielectric Constant | 3.7 @Frequency 1.00e+6 Hz |
3.7 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 3.9 @Frequency 100 Hz |
3.9 @Frequency 100 Hz |
IEC 60250 | |
| 4.1 @Frequency 1.00e+6 Hz |
4.1 @Frequency 1.00e+6 Hz |
Conditioned; IEC 60250 | |
| 8.7 @Frequency 100 Hz |
8.7 @Frequency 100 Hz |
Conditioned; IEC 60250 | |
| Dielectric Strength | 34.8 kV/mm | 884 kV/in | Conditioned; IEC 60243-1 |
| 38.5 kV/mm | 978 kV/in | IEC 60243-1 | |
| Dissipation Factor | 0.0080 @Frequency 100 Hz |
0.0080 @Frequency 100 Hz |
IEC 60250 |
| 0.012 @Frequency 1.00e+6 Hz |
0.012 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| 0.070 @Frequency 1.00e+6 Hz |
0.070 @Frequency 1.00e+6 Hz |
Conditioned; IEC 60250 | |
| 0.13 @Frequency 100 Hz |
0.13 @Frequency 100 Hz |
Conditioned; IEC 60250 | |
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Form | Pellets | |
| ISO Shortname | ISO 1874-PA 66,MFR,10-100,GF30; ISO 1043 PA GF FR (30+40) | |
| Processing | Injection molding | |
| Region | Asia Pacific | |
| Europe | ||
| Near East/Africa | ||
| North America | ||
| South and Central America |
Users viewing this material also viewed the following:
- Polimeri Europa Europrene Latice® 5585 Carboxylated Styrene - Butadiene Copolymer
- Industrial Laminates/Norplex NP555 Carbon Fiber (discontinued **)
- Lucobit Lucobatch® 1850 T100 Polyolefin TPO Granules
- SABIC Innovative Plastics LNP THERMOCOMP PX85100 PA 6
- A. Schulman FORMION™ FI 391 Ionomer
- Unitika U-100 Engineering Plastic
- DuPont Performance Polymers Delrin® 300PE NC010 Acetal (POM) (Unverified Data**)
- Denka TE-20 Transparent Resin Polymer (MABS resin) ABS
- Dow DX5E66 Polypropylene Resin
- SABIC Innovative Plastics Lexan® 950A PC
Copyright © lookpolymers.com All Rights Reserved