Huntsman IROGRAN® A 87 P 4946 TPU-Polyester
| Category | Polymer , Thermoplastic , Polyurethane, TP , Thermoplastic Polyurethane (TPUR), Polyester Grade |
| Manufacturer | Huntsman Corporation |
| Trade Name | IROGRAN® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Huntsman IROGRAN® A 87 P 4946 TPU-Polyester.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Introduction: IROGRAN A 87 P 4946 is a polyether based thermoplastic polyurethane intended for injection molding and extrusion applications. IROGRAN A 87 P 4946 is part of the HUNTSMAN technical extrusion product range and offers a specially designed, flexible material with high extrudability.Performance Features: High microbial resistance Excellent hydrolysis resistance High stability of melt High production rateInformation provided by Alliance Polymers
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.12 g/cc | 0.0405 lb/in³ | Injection molded parts; ASTM D792 |
| Linear Mold Shrinkage | 0.0080 cm/cm | 0.0080 in/in | Injection molded; ASTM D955 |
| Melt Index of Compound | 65 g/10 min @Load 21.6 kg, Temperature 190 °C |
65 g/10 min @Load 47.6 lb, Temperature 374 °F |
MVR, [cm<sup>3</sup>/10 min] |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 87 | 87 | Injection molded parts; ASTM D2240 |
| Hardness, Shore D | 38 | 38 | Injection molded parts; ASTM D2240 |
| Tensile Strength at Break | 40.0 MPa | 5800 psi | Injection molded parts; DIN 53504 |
| Elongation at Break | 650 % | 650 % | Injection molded parts; DIN 53504 |
| 100% Modulus | 0.00700 GPa | 1.02 ksi | Injection molded parts; DIN 53504 |
| 300% Modulus | 0.0110 GPa | 1.60 ksi | Injection molded parts; DIN 53504 |
| Tear Strength | 98.2 kN/m | 560 pli | Injection molded parts; ASTM D624 |
| Abrasion | 35 | 35 | mm<sup>3</sup>, Injection molded; ISO 4649 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 25.0 - 35.0 °C | 77.0 - 95.0 °F | Injection |
| 25.0 - 40.0 °C | 77.0 - 104 °F | Extrusion | |
| Middle Barrel Temperature | 175 - 185 °C | 347 - 365 °F | Extrusion |
| Nozzle Temperature | 180 - 190 °C | 356 - 374 °F | Extrusion |
| 185 - 200 °C | 365 - 392 °F | Injection | |
| Adapter Temperature | 185 - 195 °C | 365 - 383 °F | Extrusion |
| Die Temperature | 185 - 195 °C | 365 - 383 °F | Extrusion |
| Mold Temperature | 20.0 - 50.0 °C | 68.0 - 122 °F | Injection |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Heating Zone | 185-195°C | Injection |
Users viewing this material also viewed the following:
- PTS Trilac® ABS-EX1000 High Impact Extrusion Grade ABS Resin
- NOVA Chemicals Novapol® TF-0119-F Hexene LLDPE Film Resin
- Overview of materials for Polycarbonate/ABS Alloy, NCG Fiber Filled
- LG Chemical SEETEC EF320 Ethylene Vinyl Acetate
- Solvay Specialty Polymers Ryton® QC220N Polyphenylene Sulfide (PPS)
- Techmer ES HiFill® PA6 GF20 L UV 20% Glass Filled
- SABIC Innovative Plastics LNP THERMOCOMP KF008 Acetal Copolymer (Europe-Africa-Middle East)
- SMAC SMACDISK® 1114S Damping Material
- AK Steel 435 Mod Ferritic Stainless steel
- Chevron Phillips Marlex® 9518H High Density Polyethylene, Blow Molding
Copyright © lookpolymers.com All Rights Reserved