Lanxess Durethan® BKV 35 H2.0 EF 901510 Nylon 6, 35% Glass Fiber
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 40% Glass Fiber Filled |
| Manufacturer | Lanxess |
| Trade Name | Durethan® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Durethan® BKV 35 H2.0 EF 901510 Nylon 6, 35% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PA 6, injection molding grade, 35% glass fibers, good heat-ageing resistance, good flowability (easy flow)
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.40 g/cc | 0.0506 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0021 cm/cm | 0.0021 in/in | ISO 294-4, 2577 |
| Linear Mold Shrinkage, Transverse | 0.0060 cm/cm | 0.0060 in/in | ISO 294-4, 2577 |
| Melt Flow | 60 g/10 min @Load 5.00 kg, Temperature 260 °C |
60 g/10 min @Load 11.0 lb, Temperature 500 °F |
Estimated using room temperature density; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 115 MPa | 16700 psi | Conditioned; ISO 527-1/-2 |
| 190 MPa | 27600 psi | ISO 527-1/-2 | |
| Elongation at Break | 3.0 % | 3.0 % | ISO 527-1/-2 |
| 6.0 % | 6.0 % | Conditioned; ISO 527-1/-2 | |
| Tensile Modulus | 6.70 GPa | 972 ksi | Conditioned; ISO 527-1/-2 |
| 10.5 GPa | 1520 ksi | ISO 527-1/-2 | |
| Charpy Impact Unnotched | 5.50 J/cm² @Temperature -30.0 °C |
26.2 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU |
| 5.50 J/cm² @Temperature -30.0 °C |
26.2 ft-lb/in² @Temperature -22.0 °F |
Conditioned; ISO 179/1eU | |
| 7.00 J/cm² @Temperature 23.0 °C |
33.3 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |
| 8.00 J/cm² @Temperature 23.0 °C |
38.1 ft-lb/in² @Temperature 73.4 °F |
Conditioned; ISO 179/1eU | |
| Charpy Impact, Notched | 1.00 J/cm² @Temperature 23.0 °C |
4.76 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| 1.50 J/cm² @Temperature 23.0 °C |
7.14 ft-lb/in² @Temperature 73.4 °F |
Conditioned; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 30.0 µm/m-°C | 16.7 µin/in-°F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 90.0 µm/m-°C | 50.0 µin/in-°F | ISO 11359-1/-2 |
| Melting Point | 220 °C | 428 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | ISO 75-1/-2 |
| Deflection Temperature at 8.0 MPa | 160 °C | 320 °F | ISO 75-1/-2 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Additives | Release agent | |
| Features | Heat stabilized or stable to heat | |
| Form | Pellets | |
| ISO Shortname | ISO1874-PA6, MHR, 10-100, GF35 | |
| Processing | Injection molding | |
| Region | Asia Pacific | |
| Europe | ||
| Near East/Africa | ||
| North America | ||
| South and Central America |
Users viewing this material also viewed the following:
- Nabaltec GRANALOX® NM 9622 B Ceramic Body, Binder Free
- Pau Tai Unistab BC-541 Mixed Metal Liquid Stabilizer for PVC Cadmium/Barium/Zinc Self-Lubricating
- SABIC Innovative Plastics LNP LUBRICOMP KL002 Acetal Copoly
- Styron DL 460NA SB Latex
- Shakespeare LMX-3 Easy Casting Nylon Copolymer Fishing Line, 6 lb
- Unifrax Fiberfrax® Square Braid
- Master Bond EP35 High Temperature Resistant Two Component Epoxy System
- ChevronTexaco ISO 460 AIO
- Arlon RBLW401R##-P1 0.040" (1.02 mm) Cured Self-Fusing Silicone Rubber
Copyright © lookpolymers.com All Rights Reserved