Lanxess Durethan® BKV 230 H2.0 DUS008 000000 Nylon 6, 30% Glass Fiber

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled
Manufacturer Lanxess
Trade Name Durethan®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Lanxess Durethan® BKV 230 H2.0 DUS008 000000 Nylon 6, 30% Glass Fiber.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PA 6, 30% glass fibersInformation provided by LANXESS.
Physical Properties Metric English Comments
Density 1.32 g/cc
0.0477 lb/in³
ISO 1183
Linear Mold Shrinkage, Flow 0.0035 cm/cm
0.0035 in/in
60x60x2; 280°C / MT 80°C; 600 bar; ISO 2577
Linear Mold Shrinkage, Transverse 0.0085 cm/cm
0.0085 in/in
60x60x2; 280°C / MT 80°C; 600 bar; ISO 2577
Mechanical Properties Metric English Comments
Tensile Strength at Break 85.0 MPa
12300 psi
conditioned, 5 mm/min; ISO 527-1,-2
130 MPa
18900 psi
5 mm/min; ISO 527-1,-2
Elongation at Break 3.5 %
3.5 %
5 mm/min; ISO 527-1,-2
8.0 %
8.0 %
conditioned, 5 mm/min; ISO 527-1,-2
Tensile Modulus 4.40 GPa
638 ksi
conditioned, 1 mm/min; ISO 527-1,-2
8.60 GPa
1250 ksi
1 mm/min; ISO 527-1,-2
Flexural Strength 125 MPa
18100 psi
conditioned, 2 mm/min; ISO 178-A
210 MPa
30500 psi
2 mm/min; ISO 178-A
Flexural Modulus 4.40 GPa
638 ksi
conditioned, 2 mm/min; ISO 178-A
7.50 GPa
1090 ksi
2 mm/min; ISO 178-A
Izod Impact, Notched (ISO) 14.0 kJ/m²

@Temperature -30.0 °C
 6.66 ft-lb/in²

@Temperature -22.0 °F
 ISO 180-1A
15.0 kJ/m²

@Temperature -30.0 °C
 7.14 ft-lb/in²

@Temperature -22.0 °F
 conditioned; ISO 180-1A
23.0 kJ/m²

@Temperature 23.0 °C
 10.9 ft-lb/in²

@Temperature 73.4 °F
 ISO 180-1A
35.0 kJ/m²

@Temperature 23.0 °C
 16.7 ft-lb/in²

@Temperature 73.4 °F
 conditioned; ISO 180-1A
Izod Impact, Unnotched (ISO) 75.0 kJ/m²

@Temperature 23.0 °C
 35.7 ft-lb/in²

@Temperature 73.4 °F
 ISO 180-1U
75.0 kJ/m²

@Temperature -30.0 °C
 35.7 ft-lb/in²

@Temperature -22.0 °F
 ISO 180-1U
75.0 kJ/m²

@Temperature -30.0 °C
 35.7 ft-lb/in²

@Temperature -22.0 °F
 conditioned; ISO 180-1U
90.0 kJ/m²

@Temperature 23.0 °C
 42.8 ft-lb/in²

@Temperature 73.4 °F
 conditioned; ISO 180-1U
Thermal Properties Metric English Comments
Melting Point 220 °C
428 °F
10 °C/min; ISO 11357-1,-3
Deflection Temperature at 0.46 MPa (66 psi) 218 °C
424 °F
ISO 75-1,-2
Deflection Temperature at 1.8 MPa (264 psi) 198 °C
388 °F
ISO 75-1,-2
Shrinkage 0.0400 %

@Temperature 120 °C,
Time 14400 sec
 0.0400 %

@Temperature 248 °F,
Time 4.00 hour
 post-shrinkage, transverse, 60x60x2; ISO 2577
0.140 %

@Temperature 120 °C,
Time 14400 sec
 0.140 %

@Temperature 248 °F,
Time 4.00 hour
 post-shrinkage, 60x60x2; ISO 2577
Processing Properties Metric English Comments
Melt Temperature 280 °C
536 °F
Injection molding; ISO 294
Mold Temperature 80.0 °C
176 °F
Injection molding; ISO 294
Dry Time 2.00 - 6.00 hour

@Temperature 80.0 °C
 2.00 - 6.00 hour

@Temperature 176 °F
Moisture Content 0.030 - 0.12 %
0.030 - 0.12 %
Karl Fischer test