- Lanxess Durethan® BKV 130 H2.0 901510 Copolyamide, 30% Glass Fiber
Lanxess Durethan® BKV 130 H2.0 901510 Copolyamide, 30% Glass Fiber
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | Lanxess |
| Trade Name | Durethan® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Durethan® BKV 130 H2.0 901510 Copolyamide, 30% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
CoPA, injection molding grade, 30% glass fibers, elastomer-modified, electroplateable, improved notched impact strength and energy absorption under biaxial impact load, good heat-ageing resistance
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.36 g/cc | 0.0491 lb/in³ | ISO 1183 |
| Water Absorption | 7.0 % | 7.0 % | Test Sim. to ISO 62 |
| Moisture Absorption at Equilibrium | 2.0 % | 2.0 % | 23°C/50% R.H.; Test Sim. to ISO 62 |
| Viscosity Test | 134 cm³/g | 134 cm³/g | Viscosity number; ISO 307, 1157, 1628 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 100 MPa | 14500 psi | Conditioned; ISO 527-1/-2 |
| 160 MPa | 23200 psi | ISO 527-1/-2 | |
| Elongation at Break | 3.0 % | 3.0 % | ISO 527-1/-2 |
| 8.0 % | 8.0 % | Conditioned; ISO 527-1/-2 | |
| Tensile Modulus | 5.10 GPa | 740 ksi | Conditioned; ISO 527-1/-2 |
| 9.20 GPa | 1330 ksi | ISO 527-1/-2 | |
| Charpy Impact Unnotched | 7.00 J/cm² @Temperature -30.0 °C |
33.3 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU |
| 7.50 J/cm² @Temperature -30.0 °C |
35.7 ft-lb/in² @Temperature -22.0 °F |
Conditioned; ISO 179/1eU | |
| 8.50 J/cm² @Temperature 23.0 °C |
40.4 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |
| 9.00 J/cm² @Temperature 23.0 °C |
42.8 ft-lb/in² @Temperature 73.4 °F |
Conditioned; ISO 179/1eU | |
| Charpy Impact, Notched | 1.00 J/cm² @Temperature -30.0 °C |
4.76 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| 1.00 J/cm² @Temperature -30.0 °C |
4.76 ft-lb/in² @Temperature -22.0 °F |
Conditioned; ISO 179/1eA | |
| 1.80 J/cm² @Temperature 23.0 °C |
8.57 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA | |
| 2.50 J/cm² @Temperature 23.0 °C |
11.9 ft-lb/in² @Temperature 73.4 °F |
Conditioned; ISO 179/1eA | |
| Impact | 1002 | 1002 | Puncture maximum force (N); ISO 6603-2 |
| 840 @Temperature -30.0 °C |
840 @Temperature -22.0 °F |
Puncture maximum force (N); ISO 6603-2 | |
| Puncture Energy | 9.00 J | 6.64 ft-lb | ISO 6603-2 |
| 17.0 J | 12.5 ft-lb | Conditioned; ISO 6603-2 | |
| 6.00 J @Temperature -30.0 °C |
4.43 ft-lb @Temperature -22.0 °F |
ISO 6603-2 | |
| 6.00 J @Temperature -30.0 °C |
4.43 ft-lb @Temperature -22.0 °F |
Conditioned; ISO 6603-2 | |
| Tensile Creep Modulus, 1 hour | 4200 MPa | 609000 psi | ISO 899-1 |
| Tensile Creep Modulus, 1000 hours | 3300 MPa | 479000 psi | ISO 899-1 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 20.0 µm/m-°C | 11.1 µin/in-°F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 90.0 µm/m-°C | 50.0 µin/in-°F | ISO 11359-1/-2 |
| Melting Point | 213 °C | 415 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | ISO 75-1/-2 |
| Vicat Softening Point | 200 °C | 392 °F | 50°C/h 50N; ISO 306 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
IEC 60695-11-10 |
| HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
IEC 60695-11-10 | |
| Oxygen Index | 22 % | 22 % | ISO 4589-1/-2 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | Conditioned; IEC 60093 |
| 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 | |
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | IEC 60093 |
| Dielectric Constant | 4.0 @Frequency 1.00e+6 Hz |
4.0 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 4.0 @Frequency 100 Hz |
4.0 @Frequency 100 Hz |
IEC 60250 | |
| 5.0 @Frequency 1.00e+6 Hz |
5.0 @Frequency 1.00e+6 Hz |
Conditioned; IEC 60250 | |
| 10 @Frequency 100 Hz |
10 @Frequency 100 Hz |
Conditioned; IEC 60250 | |
| Dielectric Strength | 35.0 kV/mm | 889 kV/in | Conditioned; IEC 60243-1 |
| 40.0 kV/mm | 1020 kV/in | IEC 60243-1 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Additives | Release agent | |
| Features | Heat stabilized or stable to heat | |
| High impact or high impact modified | ||
| Form | Pellets | |
| ISO Shortname | ISO 1874-PA 6/66-I, MHR, 14-090, GF30 | |
| Processing | Injection molding | |
| Region | Asia Pacific | |
| Europe | ||
| Near East/Africa | ||
| North America | ||
| South and Central America |
Users viewing this material also viewed the following:
- Murtfeldt Murytal® C Blue [FS] Acetal Copolymer
- Plastcom SLOVASTER® B1 BT TS PBT, basic type
- Outokumpu 153MA™ High Temperature Austenitic Stainless Steel
- SABIC Innovative Plastics LNP LUBRICOMP Lexan_WR5210R PC (Europe-Africa-Middle East)
- Sterigenics Raprex® R200D Branched High Density Polyethylene
- A. Schulman FORMION™ FI 120 Non-Reinforced, Injection Molding Grade Zinc Ionomer
- DSM Arnite® T06 200 PBT (European and Asian Grade)
- Azoty Tarnow™ TARFLEN SM-G15 PTFE
- LATI Latiohm 52/11-10 PD02 PP Homopolymer
- DuPont Performance Polymers Delrin® 527UV NC010 Acetal Homopolymer (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved