- Lanxess Durethan® BKV 115 DUS008 000000 Nylon 6, 15% Glass Fiber
Lanxess Durethan® BKV 115 DUS008 000000 Nylon 6, 15% Glass Fiber
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 20% Glass Fiber Filled , Nylon 6, Glass Filled, Impact Grade , Nylon 6, Heat Stabilized |
| Manufacturer | Lanxess |
| Trade Name | Durethan® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Durethan® BKV 115 DUS008 000000 Nylon 6, 15% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PA 6, 15% glass fibers, injection molding, impact modified, heat-ageing stabilizedInformation provided by LANXESS.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.228 g/cc | 0.04436 lb/in³ | ISO 1183 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 65.0 MPa | 9430 psi | conditioned, 5 mm/min; ISO 527-1,-2 |
| 115 MPa | 16700 psi | 5 mm/min; ISO 527-1,-2 | |
| Elongation at Break | 4.0 % | 4.0 % | 5 mm/min; ISO 527-1,-2 |
| 14 % | 14 % | conditioned, 5 mm/min; ISO 527-1,-2 | |
| Tensile Modulus | 2.80 GPa | 406 ksi | conditioned, 1 mm/min; ISO 527-1,-2 |
| 5.60 GPa | 812 ksi | 1 mm/min; ISO 527-1,-2 | |
| Flexural Strength | 95.0 MPa | 13800 psi | conditioned, 2 mm/min; ISO 178-A |
| 185 MPa | 26800 psi | 2 mm/min; ISO 178-A | |
| Flexural Modulus | 2.50 GPa | 363 ksi | conditioned, 2 mm/min; ISO 178-A |
| 4.90 GPa | 711 ksi | 2 mm/min; ISO 178-A | |
| Charpy Impact Unnotched | 5.00 J/cm² @Temperature -30.0 °C |
23.8 ft-lb/in² @Temperature -22.0 °F |
ISO 179-1eU |
| 6.50 J/cm² @Temperature 23.0 °C |
30.9 ft-lb/in² @Temperature 73.4 °F |
ISO 179-1eU | |
| 8.00 J/cm² @Temperature 23.0 °C |
38.1 ft-lb/in² @Temperature 73.4 °F |
conditioned; ISO 179-1eU | |
| Charpy Impact, Notched | <= 1.00 J/cm² @Temperature 23.0 °C |
<= 4.76 ft-lb/in² @Temperature 73.4 °F |
ISO 179-1eA |
| 1.00 J/cm² @Temperature -30.0 °C |
4.76 ft-lb/in² @Temperature -22.0 °F |
ISO 179-1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 220 °C | 428 °F | 10 °C/min; ISO 11357-1,-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 215 °C | 419 °F | ISO 75-1,-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 195 °C | 383 °F | ISO 75-1,-2 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 280 °C | 536 °F | Injection molding; ISO 294 |
| Mold Temperature | 80.0 °C | 176 °F | Injection molding; ISO 294 |
| Dry Time | 2.00 - 6.00 hour @Temperature 80.0 °C |
2.00 - 6.00 hour @Temperature 176 °F |
|
| Moisture Content | 0.030 - 0.12 % | 0.030 - 0.12 % | residual; Karl Fischer test |
Users viewing this material also viewed the following:
- MV Labs RU490 [Ru(C10H8N2)3]Cl2·6H2O Tris(2,2'-bipyridyl)dichlororuthenium(II) dichloride hexahydrate
- Permabond 105 Cyanoacrylate, for difficult rubbers
- PolyOne Bergamid™ A70 G35 UF SO Polyamide 66 (Nylon 66)
- Solvay Specialty Polymers Hyflon® PFA 450 Fluoropolymer (discontinued **)
- Global GG-3245 High Density Polyethylene, Blow Molding Grade
- Techmer ES HiFill® PA6/6 GF/M40 HS Up BK 40% Glass/Mineral Fiber Filled
- SABIC Innovative Plastics LNP THERMOCOMP ZF0049 PPE+PS (Asia Pacific)
- E-Polymers SEPAZ® V335HS 35% Glass Fiber Reinforced Heat Stabilized PPA
- 3M Scotch® 720 Film/Fiber Tape
- Ashley Polymers Ashlene® 830LN Nylon 6
Copyright © lookpolymers.com All Rights Reserved