Lanxess Durethan® BC 550 DUSXBL 900116 Nylon 6

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Heat Stabilized , Nylon 6, Impact Grade , Nylon 6, Unreinforced
Manufacturer Lanxess
Trade Name Durethan®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Lanxess Durethan® BC 550 DUSXBL 900116 Nylon 6.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PA 6, non-reinforced, extrusion, Blastorm, impact modified, heat-ageing stabilizedInformation provided by LANXESS.
Physical Properties Metric English Comments
Density 1.07 g/cc
0.0387 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 2.4 %
2.4 %
50% RH; ISO 62
Water Absorption at Saturation 9.8 %
9.8 %
ISO 62
Linear Mold Shrinkage, Flow 0.013 cm/cm
0.013 in/in
60x60x2; 260°C / MT 80°C; 600 bar; ISO 294-4
Linear Mold Shrinkage, Transverse 0.015 cm/cm
0.015 in/in
60x60x2; 260°C / MT 80°C; 600 bar; ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength at Break 50.0 MPa
7250 psi
at yield, 50 mm/min; ISO 527-1,-2
Elongation at Break 110 %
110 %
50 mm/min; ISO 527-1,-2
Elongation at Yield 3.8 %
3.8 %
50 mm/min; ISO 527-1,-2
Tensile Modulus 0.470 GPa
68.2 ksi
conditioned, 1 mm/min; ISO 527-1,-2
2.00 GPa
290 ksi
1 mm/min; ISO 527-1,-2
Flexural Strength 20.0 MPa
2900 psi
conditioned, 2 mm/min; ISO 178-A
70.0 MPa
10200 psi
2 mm/min; ISO 178-A
Flexural Modulus 0.470 GPa
68.2 ksi
conditioned, 2 mm/min; ISO 178-A
1.80 GPa
261 ksi
2 mm/min; ISO 178-A
Izod Impact, Notched (ISO) 20.0 kJ/m²

@Temperature -30.0 °C
 9.52 ft-lb/in²

@Temperature -22.0 °F
 ISO 180-1A
75.0 kJ/m²

@Temperature 23.0 °C
 35.7 ft-lb/in²

@Temperature 73.4 °F
 ISO 180-1A
100 kJ/m²

@Temperature 23.0 °C
 47.6 ft-lb/in²

@Temperature 73.4 °F
 conditioned; ISO 180-1A
Charpy Impact, Notched 2.00 J/cm²

@Temperature -30.0 °C
 9.52 ft-lb/in²

@Temperature -22.0 °F
 ISO 179-1eA
9.00 J/cm²

@Temperature 23.0 °C
 42.8 ft-lb/in²

@Temperature 73.4 °F
 ISO 179-1eA
13.0 J/cm²

@Temperature 23.0 °C
 61.9 ft-lb/in²

@Temperature 73.4 °F
 conditioned; ISO 179-1eA
Puncture Energy 64.0 J

@Temperature 23.0 °C
 47.2 ft-lb

@Temperature 73.4 °F
 ISO 6603-2
64.0 J

@Temperature -30.0 °C
 47.2 ft-lb

@Temperature -22.0 °F
 ISO 6603-2
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 150 µm/m-°C

@Temperature 23.0 - 55.0 °C
 83.3 µin/in-°F

@Temperature 73.4 - 131 °F
 ISO 11359-1,-2
CTE, linear, Transverse to Flow 150 µm/m-°C

@Temperature 23.0 - 55.0 °C
 83.3 µin/in-°F

@Temperature 73.4 - 131 °F
 ISO 11359-1,-2
Melting Point 220 °C
428 °F
10 °C/min; ISO 11357-1,-3
Deflection Temperature at 0.46 MPa (66 psi) 95.0 °C
203 °F
ISO 75-1,-2
Deflection Temperature at 1.8 MPa (264 psi) 53.0 °C
127 °F
ISO 75-1,-2
Shrinkage 0.100 %

@Temperature 120 °C,
Time 14400 sec
 0.100 %

@Temperature 248 °F,
Time 4.00 hour
 post-shrinkage, transverse, 60x60x2; ISO 294-4
0.200 %

@Temperature 120 °C,
Time 14400 sec
 0.200 %

@Temperature 248 °F,
Time 4.00 hour
 post-shrinkage, 60x60x2; ISO 294-4
Processing Properties Metric English Comments
Melt Temperature 260 °C
500 °F
Injection molding; ISO 294
Mold Temperature 80.0 °C
176 °F
Injection molding; ISO 294
Dry Time 2.00 - 6.00 hour

@Temperature 80.0 °C
 2.00 - 6.00 hour

@Temperature 176 °F
Moisture Content 0.00 - 0.060 %
0.00 - 0.060 %
residual; Karl Fischer test