- LTL Color Compounds ColorFast® JCT1000 Polycarbonate-ABS-SMA Alloy
LTL Color Compounds ColorFast® JCT1000 Polycarbonate-ABS-SMA Alloy
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) , SMA Polymer |
| Manufacturer | LTL Color Compounds |
| Trade Name | ColorFast® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LTL Color Compounds ColorFast® JCT1000 Polycarbonate-ABS-SMA Alloy.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Unique PC/ABS/SMA alloy with improved processing and reduced plate-outAll information provided by LTL Color Compounders, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.19 g/cc | 1.19 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0040 - 0.0060 cm/cm | 0.0040 - 0.0060 in/in | 0.125; ASTM D955 |
| Melt Flow | 14 g/10 min @Load 2.16 kg, Temperature 260 °C |
14 g/10 min @Load 4.76 lb, Temperature 500 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 122 | 122 | ASTM D785 |
| Tensile Strength at Break | 55.8 MPa | 8100 psi | 2.0 in/min; ASTM D638 |
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | 2.0 in/min; ASTM D638 |
| Elongation at Break | 90 % | 90 % | 2.0 in/min; ASTM D638 |
| Elongation at Yield | 4.0 % | 4.0 % | 2.0 in/min; ASTM D638 |
| Flexural Strength | 95.1 MPa | 13800 psi | 2.0 in/min; ASTM D790 |
| Flexural Modulus | 2.70 GPa | 392 ksi | 2.0 in/min; ASTM D790 |
| Izod Impact, Notched | 6.41 J/cm @Temperature 22.8 °C |
12.0 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 95.0 °C | 203 °F | Unannealed (0.250"); ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 210 - 254 °C | 410 - 490 °F | |
| Middle Barrel Temperature | 216 - 260 °C | 420 - 500 °F | |
| Front Barrel Temperature | 227 - 274 °C | 440 - 525 °F | |
| Nozzle Temperature | 232 - 274 °C | 450 - 525 °F | |
| Melt Temperature | 232 - 274 °C | 450 - 525 °F | |
| Mold Temperature | 60.0 - 82.2 °C | 140 - 180 °F | |
| Drying Temperature | 82.2 °C | 180 °F | |
| Dry Time | 3 - 4 hour | 3 - 4 hour | nominal; maximum drying time of 8 hours |
| Back Pressure | 0.345 - 0.689 MPa | 50.0 - 100 psi | |
| Shot Size | 30 - 60 % | 30 - 60 % | |
| Vent Depth | 0.00381 - 0.00762 cm | 0.00150 - 0.00300 in | |
| Screw Speed | 30 - 75 rpm | 30 - 75 rpm |
Users viewing this material also viewed the following:
- Karina E 670D10/116-Y White PVC Compound
- Taiwan PU Corporation TPU-BH85 Hydrolysis Resistance, Blow Molding Polyether Base TPU
- Styrolution PS 485N HIPS
- Chevron Phillips K-Resin® KK38 Styrene-Butadiene Copolymer, Sheet Grade
- ChevronTexaco Vistac® ISO 68 Way Oil D
- Dow Nordel® IP 5565 Dense Extruded Profile
- Aclo Accutech Polypropylene Copolymer CP0437M20L Mica Reinforced
- Arkema Group EVATANE® 28-05 Copolymer Ethylene - Vinyl Acetate
- Teknor Apex APEX® 3050-H Polyvinyl Chloride, Flexible
Copyright © lookpolymers.com All Rights Reserved