LTL Color Compounds ColorFast® FRPC310 Polycarbonate, Flame-Retarded
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Glass Fiber Filled, Flame Retardant |
| Manufacturer | LTL Color Compounds |
| Trade Name | ColorFast® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LTL Color Compounds ColorFast® FRPC310 Polycarbonate, Flame-Retarded.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
V0-rated 10% glass-filled polycarbonate, excellent impact strengthAll information provided by LTL Color Compounders, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.27 g/cc | 1.27 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0020 - 0.0040 cm/cm | 0.0020 - 0.0040 in/in | 0.125; ASTM D955 |
| Melt Flow | 9.0 g/10 min @Load 1.20 kg, Temperature 300 °C |
9.0 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 85 | 85 | ASTM D785 |
| Tensile Strength at Break | 55.2 MPa | 8000 psi | 2.0 in/min; ASTM D638 |
| Tensile Strength, Yield | 66.2 MPa | 9600 psi | 2.0 in/min; ASTM D638 |
| Elongation at Break | 15 % | 15 % | 2.0 in/min; ASTM D638 |
| Elongation at Yield | 8.0 % | 8.0 % | 2.0 in/min; ASTM D638 |
| Flexural Strength | 103 MPa | 15000 psi | 2.0 in/min; ASTM D790 |
| Flexural Modulus | 3.45 GPa | 500 ksi | 2.0 in/min; ASTM D790 |
| Izod Impact, Notched | 1.07 J/cm @Temperature 22.8 °C |
2.00 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 142 °C | 288 °F | Unannealed (0.250"); ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
|
| 5VA @Thickness 3.00 mm |
5VA @Thickness 0.118 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 288 - 310 °C | 550 - 590 °F | |
| Middle Barrel Temperature | 299 - 321 °C | 570 - 610 °F | |
| Front Barrel Temperature | 310 - 332 °C | 590 - 630 °F | |
| Nozzle Temperature | 304 - 327 °C | 580 - 620 °F | |
| Melt Temperature | 310 - 332 °C | 590 - 630 °F | |
| Mold Temperature | 82.2 - 116 °C | 180 - 240 °F | |
| Drying Temperature | 121 °C | 250 °F | |
| Dry Time | 3 - 4 hour | 3 - 4 hour | nominal; maximum drying time of 48 hours |
| Back Pressure | 0.345 - 0.689 MPa | 50.0 - 100 psi | |
| Shot Size | 40 - 60 % | 40 - 60 % | |
| Vent Depth | 0.00254 - 0.00762 cm | 0.00100 - 0.00300 in | |
| Screw Speed | 40 - 70 rpm | 40 - 70 rpm |
| Descriptive Properties | Value | Comments |
|---|---|---|
| UL File Number | E178307 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® FXD103R PC (Asia Pacific)
- Michelman® Michem® Coat 40Y Water resistant, cold set and hot melt gluable coating
- Indium Corp. 16-1081 Flux Thinner
- Spartech CastAlloy Weatherable Sheet
- ExxonMobil 25 Mobil DTE 20 Series
- A. Schulman SCHULADUR® A GF20HI 20% Glass Fiber Reinforced, High Impact PBT
- Trimay® Wear Plate TWP170 Flux Cored Weld Wire & Electrode
- DSM Stanyl® TW341-J PA46
- ExxonMobil 412 Mobilgard 12 Series
- 3M 6035PC 12056 Polyurethane Foam Tape (20 lb./ft3 (320 kg/m3) Series)
Copyright © lookpolymers.com All Rights Reserved