LNP VALOX® SMV5845 PBT + PET Alloy, 16% Carbon Fiber Reinforcement (discontinued **)
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polyethylene Terephthalate (PET) |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LNP VALOX® SMV5845 PBT + PET Alloy, 16% Carbon Fiber Reinforcement
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
ESD Applications. Will be VC1600.Features: Good Chemical Resistance, High Flow, Flame RetardantForms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are still active under new names instituted after the SABIC purchase.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 123 MPa | 17800 psi | Type I, 5 mm/min; ASTM D638 |
| Flexural Strength | 188 MPa | 27300 psi | 102 mm Span, 3 mm/min; ASTM D790 |
| Flexural Modulus | 10.6 GPa | 1540 ksi | (102 mm Span) 3mm/min; ASTM D790 |
| Izod Impact, Notched | 0.427 J/cm | 0.800 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 202 °C @Thickness 6.35 mm |
396 °F @Thickness 0.250 in |
Unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 35 ohm-cm | 35 ohm-cm | ASTM D257 |
| Surface Resistance | 30000 ohm | 30000 ohm | ASTM D257 |
| Static Decay | <= 0.010 sec | <= 0.010 sec | 5000V to <50V; FTMS101B |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 238 - 254 °C | 460 - 489 °F | |
| Middle Barrel Temperature | 243 - 260 °C | 469 - 500 °F | |
| Front Barrel Temperature | 249 - 266 °C | 480 - 511 °F | |
| Nozzle Temperature | 243 - 260 °C | 469 - 500 °F | |
| Melt Temperature | 249 - 266 °C | 480 - 511 °F | |
| Mold Temperature | 65.6 - 87.8 °C | 150 - 190 °F | |
| Drying Temperature | 121 °C | 250 °F | |
| Dry Time | 3 - 12 hour | 3 - 12 hour | |
| Moisture Content | 0.020 % | 0.020 % | Suggested |
| Back Pressure | 0.345 - 0.689 MPa | 50.0 - 99.9 psi | |
| Clamp Pressure | 41.0 - 83.0 MPa | 5950 - 12000 psi | |
| Shot Size | 40 - 80 % | 40 - 80 % | Suggested |
| Vent Depth | 0.00250 - 0.00380 cm | 0.000984 - 0.00150 in | |
| Screw Speed | 50 - 80 rpm | 50 - 80 rpm |
Users viewing this material also viewed the following:
- PTS Trimid® N6-G15HL 15% GFR Heat Stabilized Nylon 6 with Lube
- SABIC Innovative Plastics Noryl HS2000 PPE (Asia Pacific)
- Plenco 7500 Phenolic, Granular, Compression Molded
- Polyplastics Duranex® 200FP Polybutylene Terephthalate (PBT), Unfilled PBT for film, Extrusion, Super High Flow
- A. Schulman POLYTROPE™ TPP 504 Injection Molding Grade Olefinic Thermoplastic Elastomer
- Loctite® 554 Refrigerant Sealant Thread Sealant
- ChevronTexaco ISO 220 Industrial Oil EP
- Fainplast Compounds GS 69/F Flexible PVC, Injection Molding for Footwear
- Aclo Accucomp Polyacetal (POM) ACE091L High Viscosity
- Braskem Green PE SGF4960 Blow Molding and Monofilament High Density Polyethylene
Copyright © lookpolymers.com All Rights Reserved