LNP ULTEM® SMU5852 Polyetherimide, 30% Carbon Fiber Reinforcement, 15% PTFE Lubricant (discontinued **)
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) , Polyetherimide (PEI), Carbon Fiber Filled |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LNP ULTEM® SMU5852 Polyetherimide, 30% Carbon Fiber Reinforcement, 15% PTFE Lubricant
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Features: Lubricated, Electrically Conductive, Good Wear ResistanceForms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are still active under new names instituted after the SABIC purchase.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 141 MPa | 20500 psi | Type I, 5 mm/min; ASTM D638 |
| Elongation at Break | 4.0 % | 4.0 % | Type I, 5 mm/min; ASTM D638 |
| Flexural Yield Strength | 192 MPa | 27800 psi | (102 mm Span) 3mm/min; ASTM D790 |
| Flexural Modulus | 14.1 GPa | 2050 ksi | (102 mm Span) 3mm/min; ASTM D790 |
| Izod Impact, Notched | 0.427 J/cm | 0.800 ft-lb/in | ASTM D256 |
| 2.00 J/cm | 3.75 ft-lb/in | Reverse; ASTM D256 | |
| Izod Impact, Unnotched | 3.20 J/cm | 5.99 ft-lb/in | ASTM D256 |
| Falling Dart Impact | 7.68 J | 5.66 ft-lb | ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 211 °C @Thickness 6.35 mm |
412 °F @Thickness 0.250 in |
Unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 75 ohm-cm | 75 ohm-cm | ASTM D257 |
| Surface Resistance | 5000 ohm | 5000 ohm | ASTM D257 |
| Static Decay | <= 0.010 sec | <= 0.010 sec | 5000V to <50V; FTMS101B |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 360 - 421 °C | 680 - 790 °F | |
| Middle Barrel Temperature | 371 - 421 °C | 700 - 790 °F | |
| Front Barrel Temperature | 382 - 427 °C | 720 - 801 °F | |
| Nozzle Temperature | 377 - 421 °C | 711 - 790 °F | |
| Melt Temperature | 382 - 427 °C | 720 - 801 °F | |
| Mold Temperature | 135 - 163 °C | 275 - 325 °F | |
| Drying Temperature | 149 °C | 300 °F | |
| Dry Time | <= 24 hour | <= 24 hour | |
| Moisture Content | 0.020 % | 0.020 % | Suggested |
| Back Pressure | 0.345 - 0.689 MPa | 50.0 - 99.9 psi | |
| Clamp Pressure | 41.0 - 69.0 MPa | 5950 - 10000 psi | |
| Shot Size | 40 - 60 % | 40 - 60 % | Suggested |
| Vent Depth | 0.00250 - 0.00760 cm | 0.000984 - 0.00299 in | |
| Screw Speed | 40 - 70 rpm | 40 - 70 rpm |
Users viewing this material also viewed the following:
- Parker Chomerics SOFT-SHIELD® 4850-STRIP Low-Closure Force Strip Gasket
- DSM Akulon® Ultraflow™ K-FKGS6 Nylon 6-30% Glass Reinforced (European and Asian Grade) (Dry) (discontinued **
- Lanxess Durethan® DP 1441/40 H2.0 EF 900116 Nylon 6, 40% Glass Fiber + Mineral
- Samsung Cheil Industries Starex® HF-0660IW ABS, Unreinforced
- SCG Chemicals EL-Leneâ„¢ H1000P High Density Polyethylene Pipe Resin
- Toyobo PELPRENE™ P90B Polyester TPE
- DuPont Teijin Films Mylar® RSX951 Polyester Film, 105 Gauge
- E-Polymers TEKAMID® TA250GM , GF/MF Reinforced PA66, DAM
- BASF Ultradur® B 4560 PBT
- Polykemi AB POLYfill PPH TS2040 Polypropylene Homopolymer, Mineral Reinforced
Copyright © lookpolymers.com All Rights Reserved