LG Chemical SH625 ABS, High Impact, High Flow
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Impact Grade, Molded |
| Manufacturer | LG Chemical |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | EXW, FOB, CFR, CIF |
| Payment Terms | L/C, T/T, PayPal |
| Download PDF | LG Chemical SH625 ABS, High Impact, High Flow.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Feature: Extrusion Molding, High Impact, High FlowApplication: Ski Flat, MiscellaneousCAS No. 9003-56-9Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.04 g/cc | 1.04 g/cc | ASTM D792 |
| Maximum Moisture Content | 0.010 | 0.010 | Extrusion Molding |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0070 cm/cm <br>@Thickness 3.20 mm |
0.0040 - 0.0070 in/in <br>@Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 7.0 g/10 min <br>@Load 10.0 kg,<br> Temperature 220 °C |
7.0 g/10 min <br>@Load 22.0 lb,<br> Temperature 428 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 85 | 85 | ASTM D785 |
| Tensile Strength, Yield | 34.3 MPa <br>@Thickness 3.20 mm |
4980 psi <br>@Thickness 0.126 in |
50 mm/min; ASTM D638 |
| Elongation at Break | 35 % <br>@Thickness 3.20 mm |
35 % <br>@Thickness 0.126 in |
50 mm/min; ASTM D638 |
| Elongation at Yield | >= 5.0 % <br>@Thickness 3.20 mm |
>= 5.0 % <br>@Thickness 0.126 in |
50 mm/min; ASTM D638 |
| Flexural Yield Strength | 53.9 MPa <br>@Thickness 3.20 mm |
7820 psi <br>@Thickness 0.126 in |
15 mm/min; ASTM D790 |
| Flexural Modulus | 1.81 GPa <br>@Thickness 3.20 mm |
263 ksi <br>@Thickness 0.126 in |
15 mm/min; ASTM D790 |
| Izod Impact, Notched | 4.31 J/cm <br>@Thickness 6.40 mm,<br> Temperature 23.0 °C |
8.08 ft-lb/in <br>@Thickness 0.252 in,<br> Temperature 73.4 °F |
ASTM D256 |
| 5.39 J/cm <br>@Thickness 3.20 mm,<br> Temperature 23.0 °C |
10.1 ft-lb/in <br>@Thickness 0.126 in,<br> Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 90.0 °C <br>@Thickness 6.40 mm |
194 °F <br>@Thickness 0.252 in |
Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 83.0 °C <br>@Thickness 6.40 mm |
181 °F <br>@Thickness 0.252 in |
Unannealed; ASTM D648 |
| Vicat Softening Point | 90.0 °C <br>@Load 5.00 kg |
194 °F <br>@Load 11.0 lb |
50°C/h; ASTM D1525 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Zone 1 | 180 - 210 °C | 356 - 410 °F | Extrusion Molding |
| Zone 2 | 190 - 230 °C | 374 - 446 °F | Extrusion Molding |
| Zone 3 | 200 - 250 °C | 392 - 482 °F | Extrusion Molding |
| Zone 4 | 200 - 250 °C | 392 - 482 °F | Extrusion Molding |
| Adapter Temperature | 200 - 250 °C | 392 - 482 °F | Extrusion Molding |
| Die Temperature | 200 - 250 °C | 392 - 482 °F | Extrusion Molding |
| Melt Temperature | 200 - 250 °C | 392 - 482 °F | Extrusion Molding |
| Roll Temperature | 60.0 - 90.0 °C | 140 - 194 °F | Bottom, Extrusion |
| 70.0 - 90.0 °C | 158 - 194 °F | Middle, Extrusion | |
| 70.0 - 100 °C | 158 - 212 °F | Top, Extrusion | |
| Drying Temperature | 70.0 - 80.0 °C | 158 - 176 °F | Extrusion Molding |
| Dry Time | 3.00 - 4.00 hour | 3.00 - 4.00 hour | Extrusion Molding |
Users viewing this material also viewed the following:
- Plastcom SLOVAMID 6 GF 30 LS Polyamide 6, 30% Glass Fiber, UV Stabilization
- Solvay TOLCIDE® PS 75 75% tetrakis hydroxymethyl phosphonium sulfate
- Suzhou Hipro Polymers Hiprolon® 11 PFB Colorized Nylon powder
- Borealis Daplen™ EE137AI Polypropylene Compound 10% Mineral Filled
- Chase Plastics CP Pryme® NN213GL (COND, 50% RH) Nylon 66, 13% Glass Fiber Reinforced, Internally Lubricated
- A. Schulman POLYBATCH™ U-7025-CFK Blowing Agent Concentrate Based In Polystyrene
- CoorsTek AD-90 Alumina (nom. 90% Al2O3)
- Chevron Phillips Marlex® HP132 High Density Polyethylene, Pressure Pipe Grade
Copyright © lookpolymers.com All Rights Reserved