DuPont Performance Polymers Zytel® HTN FR52G30NH BK337 Polyphthalamide (PPA)  (Unverified Data**)

Category Polymer , Thermoplastic , Polyphthalamide (PPA) , Polyphthalamide (PPA), 30% Glass Fiber Reinforced
Manufacturer DuPont Performance Polymers
Trade Name Zytel® HTN
Port Shanghai port,China
Trade Terms EXW, FOB, CFR, CIF
Payment Terms L/C, T/T, PayPal
Download PDF DuPont Performance Polymers Zytel® HTN FR52G30NH BK337 Polyphthalamide (PPA)  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
30% Glass Reinforced Flame Retardant Non-Halogenated PPA High Performance Polyamide Zytel HTNFR52G30NH BK337 is a 30% glass reinforced flame retardant lubricated high performance polyamide resin. It is also a PPA resin and it uses a non-halogenated flaInformation provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.44 g/cc
0.0520 lb/in³
DAM; ISO 1183
Linear Mold Shrinkage, Flow 0.0030 cm/cm
0.0030 in/in
DAM; ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.010 cm/cm
0.010 in/in
DAM; ISO 294-4 2577
Mechanical Properties Metric English Comments
Tensile Strength at Break 150 MPa
21800 psi
DAM; ISO 527-1/-2
Tensile Stress 0.150 MPa
<br>@Strain 0.000 %,<br> Temperature 175 °C
 21.8 psi
<br>@Strain 0.000 %,<br> Temperature 347 °F
 DAM; ISO 11403-1 -2
0.180 MPa
<br>@Strain 0.000 %,<br> Temperature 150 °C
 26.1 psi
<br>@Strain 0.000 %,<br> Temperature 302 °F
 DAM; ISO 11403-1 -2
10.49 MPa
<br>@Strain 0.200 %,<br> Temperature 150 °C
 1521 psi
<br>@Strain 0.200 %,<br> Temperature 302 °F
 50%RH; ISO 11403-1 -2
12.22 MPa
<br>@Strain 0.110 %,<br> Temperature 40.0 °C
 1772 psi
<br>@Strain 0.110 %,<br> Temperature 104 °F
 50%RH; ISO 11403-1 -2
13.56 MPa
<br>@Strain 0.110 %,<br> Temperature 23.0 °C
 1967 psi
<br>@Strain 0.110 %,<br> Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
13.67 MPa
<br>@Strain 0.110 %,<br> Temperature -40.0 °C
 1983 psi
<br>@Strain 0.110 %,<br> Temperature -40.0 °F
 50%RH; ISO 11403-1 -2
15.62 MPa
<br>@Strain 0.130 %,<br> Temperature 23.0 °C
 2265 psi
<br>@Strain 0.130 %,<br> Temperature 73.4 °F
 DAM; ISO 11403-1 -2
18.0 MPa
<br>@Strain 0.150 %,<br> Temperature -40.0 °C
 2610 psi
<br>@Strain 0.150 %,<br> Temperature -40.0 °F
 DAM; ISO 11403-1 -2
30.39 MPa
<br>@Strain 0.760 %,<br> Temperature 175 °C
 4408 psi
<br>@Strain 0.760 %,<br> Temperature 347 °F
 DAM; ISO 11403-1 -2
33.24 MPa
<br>@Strain 0.680 %,<br> Temperature 150 °C
 4821 psi
<br>@Strain 0.680 %,<br> Temperature 302 °F
 DAM; ISO 11403-1 -2
33.35 MPa
<br>@Strain 0.830 %,<br> Temperature 150 °C
 4837 psi
<br>@Strain 0.830 %,<br> Temperature 302 °F
 50%RH; ISO 11403-1 -2
44.64 MPa
<br>@Strain 0.450 %,<br> Temperature 40.0 °C
 6474 psi
<br>@Strain 0.450 %,<br> Temperature 104 °F
 50%RH; ISO 11403-1 -2
45.48 MPa
<br>@Strain 1.46 %,<br> Temperature 175 °C
 6596 psi
<br>@Strain 1.46 %,<br> Temperature 347 °F
 DAM; ISO 11403-1 -2
47.11 MPa
<br>@Strain 1.49 %,<br> Temperature 150 °C
 6833 psi
<br>@Strain 1.49 %,<br> Temperature 302 °F
 50%RH; ISO 11403-1 -2
47.7 MPa
<br>@Strain 0.420 %,<br> Temperature 23.0 °C
 6920 psi
<br>@Strain 0.420 %,<br> Temperature 73.4 °F
 DAM; ISO 11403-1 -2
48.18 MPa
<br>@Strain 0.440 %,<br> Temperature 23.0 °C
 6988 psi
<br>@Strain 0.440 %,<br> Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
49.15 MPa
<br>@Strain 1.26 %,<br> Temperature 150 °C
 7129 psi
<br>@Strain 1.26 %,<br> Temperature 302 °F
 DAM; ISO 11403-1 -2
55.18 MPa
<br>@Strain 2.30 %,<br> Temperature 175 °C
 8003 psi
<br>@Strain 2.30 %,<br> Temperature 347 °F
 DAM; ISO 11403-1 -2
55.38 MPa
<br>@Strain 2.19 %,<br> Temperature 150 °C
 8032 psi
<br>@Strain 2.19 %,<br> Temperature 302 °F
 50%RH; ISO 11403-1 -2
56.61 MPa
<br>@Strain 0.490 %,<br> Temperature -40.0 °C
 8211 psi
<br>@Strain 0.490 %,<br> Temperature -40.0 °F
 50%RH; ISO 11403-1 -2
61.01 MPa
<br>@Strain 1.99 %,<br> Temperature 150 °C
 8849 psi
<br>@Strain 1.99 %,<br> Temperature 302 °F
 DAM; ISO 11403-1 -2
61.84 MPa
<br>@Strain 0.550 %,<br> Temperature -40.0 °C
 8969 psi
<br>@Strain 0.550 %,<br> Temperature -40.0 °F
 DAM; ISO 11403-1 -2
64.29 MPa
<br>@Strain 4.64 %,<br> Temperature 150 °C
 9324 psi
<br>@Strain 4.64 %,<br> Temperature 302 °F
 50%RH; ISO 11403-1 -2
66.07 MPa
<br>@Strain 5.37 %,<br> Temperature 175 °C
 9583 psi
<br>@Strain 5.37 %,<br> Temperature 347 °F
 DAM; ISO 11403-1 -2
67.98 MPa
<br>@Strain 0.760 %,<br> Temperature 40.0 °C
 9860 psi
<br>@Strain 0.760 %,<br> Temperature 104 °F
 50%RH; ISO 11403-1 -2
71.24 MPa
<br>@Strain 0.660 %,<br> Temperature 23.0 °C
 10330 psi
<br>@Strain 0.660 %,<br> Temperature 73.4 °F
 DAM; ISO 11403-1 -2
74.37 MPa
<br>@Strain 4.87 %,<br> Temperature 150 °C
 10790 psi
<br>@Strain 4.87 %,<br> Temperature 302 °F
 DAM; ISO 11403-1 -2
74.82 MPa
<br>@Strain 0.740 %,<br> Temperature 23.0 °C
 10850 psi
<br>@Strain 0.740 %,<br> Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
85.4 MPa
<br>@Strain 1.06 %,<br> Temperature 40.0 °C
 12400 psi
<br>@Strain 1.06 %,<br> Temperature 104 °F
 50%RH; ISO 11403-1 -2
90.43 MPa
<br>@Strain 0.830 %,<br> Temperature -40.0 °C
 13120 psi
<br>@Strain 0.830 %,<br> Temperature -40.0 °F
 50%RH; ISO 11403-1 -2
91.62 MPa
<br>@Strain 0.860 %,<br> Temperature -40.0 °C
 13290 psi
<br>@Strain 0.860 %,<br> Temperature -40.0 °F
 DAM; ISO 11403-1 -2
93.25 MPa
<br>@Strain 1.00 %,<br> Temperature 23.0 °C
 13520 psi
<br>@Strain 1.00 %,<br> Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
95.43 MPa
<br>@Strain 0.950 %,<br> Temperature 23.0 °C
 13840 psi
<br>@Strain 0.950 %,<br> Temperature 73.4 °F
 DAM; ISO 11403-1 -2
116.94 MPa
<br>@Strain 1.15 %,<br> Temperature -40.0 °C
 16961 psi
<br>@Strain 1.15 %,<br> Temperature -40.0 °F
 50%RH; ISO 11403-1 -2
118.43 MPa
<br>@Strain 2.11 %,<br> Temperature 40.0 °C
 17177 psi
<br>@Strain 2.11 %,<br> Temperature 104 °F
 50%RH; ISO 11403-1 -2
119.69 MPa
<br>@Strain 1.18 %,<br> Temperature -40.0 °C
 17360 psi
<br>@Strain 1.18 %,<br> Temperature -40.0 °F
 DAM; ISO 11403-1 -2
135.95 MPa
<br>@Strain 1.94 %,<br> Temperature 23.0 °C
 19718 psi
<br>@Strain 1.94 %,<br> Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
156.87 MPa
<br>@Strain 2.06 %,<br> Temperature 23.0 °C
 22752 psi
<br>@Strain 2.06 %,<br> Temperature 73.4 °F
 DAM; ISO 11403-1 -2
178.43 MPa
<br>@Strain 2.12 %,<br> Temperature -40.0 °C
 25879 psi
<br>@Strain 2.12 %,<br> Temperature -40.0 °F
 50%RH; ISO 11403-1 -2
196.69 MPa
<br>@Strain 2.46 %,<br> Temperature -40.0 °C
 28528 psi
<br>@Strain 2.46 %,<br> Temperature -40.0 °F
 DAM; ISO 11403-1 -2
Elongation at Break 2.2 %
2.2 %
DAM; ISO 527-1/-2
Tensile Modulus 10.0 GPa
1450 ksi
DAM; ISO 527-1/-2
Flexural Strength 230 MPa
33400 psi
DAM; ISO 178
Flexural Modulus 8.70 GPa
1260 ksi
DAM; ISO 178
Secant Modulus 2.27 GPa
<br>@Strain 3.27 %,<br> Temperature 100 °C
 329 ksi
<br>@Strain 3.27 %,<br> Temperature 212 °F
 50%RH; ISO 11403-1 -2
3.04 GPa
<br>@Strain 2.27 %,<br> Temperature 100 °C
 441 ksi
<br>@Strain 2.27 %,<br> Temperature 212 °F
 50%RH; ISO 11403-1 -2
3.38 GPa
<br>@Strain 2.84 %,<br> Temperature 100 °C
 491 ksi
<br>@Strain 2.84 %,<br> Temperature 212 °F
 DAM; ISO 11403-1 -2
3.90 GPa
<br>@Strain 1.47 %,<br> Temperature 100 °C
 565 ksi
<br>@Strain 1.47 %,<br> Temperature 212 °F
 50%RH; ISO 11403-1 -2
4.38 GPa
<br>@Strain 1.95 %,<br> Temperature 100 °C
 636 ksi
<br>@Strain 1.95 %,<br> Temperature 212 °F
 DAM; ISO 11403-1 -2
5.2029 GPa
<br>@Strain 0.690 %,<br> Temperature 100 °C
 754.63 ksi
<br>@Strain 0.690 %,<br> Temperature 212 °F
 50%RH; ISO 11403-1 -2
5.36 GPa
<br>@Strain 1.24 %,<br> Temperature 100 °C
 777 ksi
<br>@Strain 1.24 %,<br> Temperature 212 °F
 DAM; ISO 11403-1 -2
5.55 GPa
<br>@Strain 2.07 %,<br> Temperature 80.0 °C
 804 ksi
<br>@Strain 2.07 %,<br> Temperature 176 °F
 DAM; ISO 11403-1 -2
6.46 GPa
<br>@Strain 1.73 %,<br> Temperature 40.0 °C
 937 ksi
<br>@Strain 1.73 %,<br> Temperature 104 °F
 50%RH; ISO 11403-1 -2
6.56 GPa
<br>@Strain 0.660 %,<br> Temperature 100 °C
 951 ksi
<br>@Strain 0.660 %,<br> Temperature 212 °F
 DAM; ISO 11403-1 -2
6.68 GPa
<br>@Strain 0.120 %,<br> Temperature 100 °C
 969 ksi
<br>@Strain 0.120 %,<br> Temperature 212 °F
 50%RH; ISO 11403-1 -2
6.70 GPa
<br>@Strain 1.46 %,<br> Temperature 80.0 °C
 971 ksi
<br>@Strain 1.46 %,<br> Temperature 176 °F
 DAM; ISO 11403-1 -2
7.4937 GPa
<br>@Strain 1.27 %,<br> Temperature 40.0 °C
 1086.9 ksi
<br>@Strain 1.27 %,<br> Temperature 104 °F
 50%RH; ISO 11403-1 -2
7.88 GPa
<br>@Strain 1.57 %,<br> Temperature 23.0 °C
 1140 ksi
<br>@Strain 1.57 %,<br> Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
7.90 GPa
<br>@Strain 0.950 %,<br> Temperature 80.0 °C
 1150 ksi
<br>@Strain 0.950 %,<br> Temperature 176 °F
 DAM; ISO 11403-1 -2
8.07 GPa
<br>@Strain 0.180 %,<br> Temperature 100 °C
 1170 ksi
<br>@Strain 0.180 %,<br> Temperature 212 °F
 DAM; ISO 11403-1 -2
Users viewing this material also viewed the following:
Copyright © lookpolymers.com All Rights Reserved