LG Chemical Lupox® LW5102F PBT+PC+GF10%
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Glass Filled , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | LG Chemical |
| Trade Name | Lupox® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical Lupox® LW5102F PBT+PC+GF10%.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Injection Molding, PBT+PC+GF10%, Low Warpage, Flame RetardantApplication: IT/OA, E&E (Switch)CAS No. 9003-01-04, 68928-70-1, 65997-17-3, 24968-12-5, 103598-77-2 and 1309-64-4Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.40 g/cc | 1.40 g/cc | ASTM D792 |
| Maximum Moisture Content | 0.020 | 0.020 | Injection Molding |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0040 - 0.0070 in/in @Thickness 0.126 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 53.9 MPa @Thickness 3.20 mm |
7820 psi @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Elongation at Break | 40 % @Thickness 3.20 mm |
40 % @Thickness 0.126 in |
5mm/min; ASTM D638 |
| Flexural Yield Strength | 90.2 MPa @Thickness 3.20 mm |
13100 psi @Thickness 0.126 in |
1.3mm/min; ASTM D790 |
| Flexural Modulus | 3.24 GPa @Thickness 3.20 mm |
469 ksi @Thickness 0.126 in |
1.3mm/min; ASTM D790 |
| Izod Impact, Notched | 0.441 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
0.827 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 225 °C | 437 °F | @ Break; ASTM D3418 |
| Deflection Temperature at 0.46 MPa (66 psi) | 190 °C @Thickness 6.40 mm |
374 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 140 °C @Thickness 6.40 mm |
284 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| UL RTI, Electrical | 75.0 °C @Thickness 1.00 - 1.10 mm |
167 °F @Thickness 0.0394 - 0.0433 in |
|
| UL RTI, Mechanical with Impact | 75.0 °C @Thickness 1.00 - 1.10 mm |
167 °F @Thickness 0.0394 - 0.0433 in |
|
| UL RTI, Mechanical without Impact | 75.0 °C @Thickness 1.00 - 1.10 mm |
167 °F @Thickness 0.0394 - 0.0433 in |
|
| Flammability, UL94 | V-0 @Thickness 1.00 - 1.10 mm |
V-0 @Thickness 0.0394 - 0.0433 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 235 - 250 °C | 455 - 482 °F | Injection Molding |
| Middle Barrel Temperature | 240 - 250 °C | 464 - 482 °F | Injection Molding |
| Front Barrel Temperature | 245 - 255 °C | 473 - 491 °F | Injection Molding |
| Nozzle Temperature | 245 - 255 °C | 473 - 491 °F | Injection Molding |
| Melt Temperature | 245 - 255 °C | 473 - 491 °F | Injection Molding |
| Mold Temperature | 60.0 - 100 °C | 140 - 212 °F | Injection Molding |
| Drying Temperature | 120 °C | 248 °F | Injection Molding |
| Dry Time | 4.00 - 6.00 hour | 4.00 - 6.00 hour | Injection Molding |
Users viewing this material also viewed the following:
- MV Labs PD460 K2PdCl6 Potassium hexachloropalladate(IV)
- RheTech Products HP800-706UV 20% Talc Reinforced High Performance Polypropylene Copolymer, Scratch Resistant, UV Stabilized, Impact Modified, SWB White
- DuPont Performance Polymers Hypalon® 20 Chlorosulfonated Polyethylene Rubber, Mineral Filled Compound (discon
- 3M Dyneon™ TF 5033 PTFE Dispersion (discontinued **)
- Overview of materials for Phenolic/Rubber; Molded
- Techmer ES HiFill® HIPS GF20 BK 20% Glass Filled
- Tisan TISSAN® Flame Retardant (V0) Styrene Acrylonitrile
- Arlon CLTE-XT High Precision Ceramic PTFE
- Carpenter O6 Graphitic Tool Steel (AISI O6)
- 3M Scotchcal™ 3650-12 Graphic Film
Copyright © lookpolymers.com All Rights Reserved