LG Chemical MI-770 MIPS
| Category | Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Impact Modified |
| Manufacturer | LG Chemical |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical MI-770 MIPS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0040 - 0.0080 cm/cm | 0.0040 - 0.0080 in/in | ASTM D955 |
| Melt Flow | 6.0 g/10 min @Load 5.00 kg, Temperature 200 °C |
6.0 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 105 | 105 | ASTM D785 |
| Tensile Strength, Yield | 36.3 MPa | 5260 psi | 50 mm/min; ASTM D638 |
| Elongation at Break | 40 % | 40 % | 50 mm/min; ASTM D638 |
| Flexural Yield Strength | 62.9 MPa | 9120 psi | 15 mm/min; ASTM D790 |
| Flexural Modulus | 2.40 GPa | 348 ksi | 15 mm/min; ASTM D790 |
| Izod Impact, Notched | 0.590 J/cm @Thickness 6.35 mm |
1.11 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| 0.780 J/cm @Thickness 3.17 mm |
1.46 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 80.0 °C @Thickness 12.7 mm |
176 °F @Thickness 0.500 in |
Unannealed; ASTM D648 |
| Vicat Softening Point | 101 °C | 214 °F | 1000 g; ASTM D1525 |
| Flammability, UL94 | HB | HB | 1/16 in |
| HB | HB | 1/8 in | |
| Flame Spread | 28.0 mm/min @Thickness 3.17 mm |
1.10 in/min @Thickness 0.125 in |
FH3 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Arc Resistance | 120 - 180 sec | 120 - 180 sec | UL Rating PLC 5 (120-180 sec) |
| Comparative Tracking Index | 400 - 600 V | 400 - 600 V | UL Rating PLC 1 (400-600 volts) |
| Hot Wire Ignition, HWI | 15 - 30 sec | 15 - 30 sec | UL Rating PLC 3 (15-30 sec) |
| High Amp Arc Ignition, HAI | >= 120 arcs | >= 120 arcs | UL Rating PLC 0 (>120 arcs) |
| High Voltage Arc-Tracking Rate, HVTR | 25.4 - 80.0 mm/min | 1.00 - 3.15 in/min | UL Rating PLC 2 (25.4-80 mm/min) |
Users viewing this material also viewed the following:
- Lehmann & Voss LUVOCOM® 1105-8432 PEEK, unreinforced
- H.C. Starck HPM 1705 Tungsten High Density Composite
- MetalTek MTEK 625 Cast UNS N26625 Severe Corrosion and Heat Resistant Alloy
- Samsung Cheil Industries Infino® HP-1000XA PC/ABS, Unreinforced
- A. Schulman POLYBATCH™ Grey 8760 Concentrate Based In Polyethylene
- ExxonMobil Mobil Clean 10W-30 7500
- Eagle Brass 102 OF COPPER (Non-Certified), Extra Hard
- Aclo Accutech Polypropylene Copolymer CP0437T10L1 Talc Reinforced
- A. Schulman POLYBATCH™ White L8350 HSF Concentrate Based In High-Flow LLDPE
Copyright © lookpolymers.com All Rights Reserved