LG Chemical Lupox® TE5100 PBT+PC+GF10%
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Glass Filled , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | LG Chemical |
| Trade Name | Lupox® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical Lupox® TE5100 PBT+PC+GF10%.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Injection Molding, PBT+PC+GF10%, High Impact resistant, Dimensional StabilityApplication: Automotive (Bumper Back Beam)CAS No. 30965-26-5, 103598-77-2 and 65997-17-3Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.29 g/cc | 1.29 g/cc | ASTM D792 |
| Maximum Moisture Content | 0.020 | 0.020 | Injection Molding |
| Linear Mold Shrinkage, Flow | 0.0070 - 0.010 cm/cm @Thickness 3.20 mm |
0.0070 - 0.010 in/in @Thickness 0.126 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 81.4 MPa @Thickness 3.20 mm |
11800 psi @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Elongation at Break | >= 6.0 % @Thickness 3.20 mm |
>= 6.0 % @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Flexural Yield Strength | 127 MPa @Thickness 6.40 mm |
18500 psi @Thickness 0.252 in |
5mm/min; ASTM D790 |
| Flexural Modulus | 3.82 GPa @Thickness 6.40 mm |
555 ksi @Thickness 0.252 in |
5mm/min; ASTM D790 |
| Izod Impact, Notched | 10.8 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
20.2 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 225 °C | 437 °F | @ Break; ASTM D3418 |
| Deflection Temperature at 1.8 MPa (264 psi) | 110 °C @Thickness 6.40 mm |
230 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 250 - 260 °C | 482 - 500 °F | Injection Molding |
| Middle Barrel Temperature | 250 - 260 °C | 482 - 500 °F | Injection Molding |
| Front Barrel Temperature | 255 - 265 °C | 491 - 509 °F | Injection Molding |
| Nozzle Temperature | 260 - 270 °C | 500 - 518 °F | Injection Molding |
| Melt Temperature | 260 - 270 °C | 500 - 518 °F | Injection Molding |
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | Injection Molding |
| Drying Temperature | 120 °C | 248 °F | Injection Molding |
| Dry Time | 4.00 - 5.00 hour | 4.00 - 5.00 hour | Injection Molding |
Users viewing this material also viewed the following:
- Multibase Multi-Flex® TPO 4308 BLK
- NOVA Chemicals Sclair® 96A HDPE Extrusion Resin (discontinued **)
- Mateck Potassium Chloride (KCl)
- Haynes Hastelloy® C-22® alloy, 12.7-50.8 mm thick bar, solution heat treated
- Techmer ES HiFill® PA6/6 GF40 UV L BK 40% Glass Filled
- Cytec Thornel® T-650/35 6K Carbon Fiber, Polyacrylonitrile (PAN) Precursor
- ExxonMobil LLDPE LLP 8360.29 Linear Low Density Polyethylene Resin
- 3M Scotchcal™ ElectroCut™ 7125-86 Graphic Film
- Overview of materials for Polyetherimide (PEI), Aramid Fiber Filled
Copyright © lookpolymers.com All Rights Reserved