Kolon KOPA® KN333G33CR G/F Reinforced Nylon 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled |
| Manufacturer | Kolon |
| Trade Name | Kopa® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Kolon KOPA® KN333G33CR G/F Reinforced Nylon 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
KOPA® is a thermoplastic resin with excellent mechanical, thermal and electrical properties and is widely used in the automobile, electrical and industrial parts.High tensile strength, outstanding self lubrication and abrasion resistance, excellent chemical & weather resistance, high usage temperatureInformation provided by US distributor, API-Kolon.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.37 g/cc | 0.0495 lb/in³ | DIN 53479; ASTM D792 |
| Water Absorption | 0.40 % | 0.40 % | DIN 53475; ASTM D570 |
| Linear Mold Shrinkage | 0.0030 - 0.0070 cm/cm | 0.0030 - 0.0070 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 121 | 121 | DIN 53505; ASTM D785 |
| Tensile Strength, Ultimate | 186 MPa | 27000 psi | DIN 53455; ASTM D638 |
| Elongation at Break | 5.5 % | 5.5 % | DIN 53455; ASTM D638 |
| Flexural Yield Strength | 284 MPa | 41200 psi | DIN 53455; ASTM D790 |
| Flexural Modulus | 9.12 GPa | 1320 ksi | DIN 53452; ASTM D790 |
| Izod Impact, Notched | 1.08 J/cm | 2.02 ft-lb/in | DIN 53453; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 20.0 µm/m-°C @Temperature 20.0 °C |
11.1 µin/in-°F @Temperature 68.0 °F |
DIN 53752; ASTM D696 |
| Melting Point | 255 °C | 491 °F | DIN 53736; ASTM D789 |
| Deflection Temperature at 0.46 MPa (66 psi) | 250 °C | 482 °F | DIN 53461; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 247 °C | 477 °F | DIN 53461; ASTM D648 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 3.6 @Frequency 1e+6 Hz |
3.6 @Frequency 1e+6 Hz |
ASTM D150/DIN 53483 |
| Dielectric Strength | 21.0 kV/mm | 533 kV/in | ASTM D149/DIN 53481 |
| Arc Resistance | 135 sec | 135 sec | ASTM D495 |
Users viewing this material also viewed the following:
- Old Hickory FC-120 Tennessee Ball Clay
- Osprey Metals 17-4 PH/MA Stainless Steel Master Alloy Powder (Grade 80% - 22)
- SABIC Innovative Plastics Lexan® DMX9455A PC Copolymer (Asia Pacific)
- Samsung Cheil Industries Starex® SD-0170 ABS, Unreinforced
- Ecomass® 1080CO94 Copper Powder Filled Polyamide Alloy, Injection Molding
- Fainplast Compounds GS 7022 Flexible PVC, Injection Molding for Footwear
- BASF Elastollan® M88A15 Polyester Type Polyurethane Elastomer
- PolyOne Edgetek® PI-10CF/000 Polyetherimide (PEI), Carbon Fiber Reinforced (discontinued **)
- Arkema Group Rilsan® BESHV Nylon 11, Blow Molding Grade (Conditioned)
Copyright © lookpolymers.com All Rights Reserved