SABIC Innovative Plastics Lexan® LCR200 PBT+PC (Asia Pacific)

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Unreinforced , Polyester, TP , Polybutylene Terephthalate (PBT)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Lexan®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Lexan® LCR200 PBT+PC (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Physical Properties Metric English Comments
Specific Gravity 1.22 g/cc
1.22 g/cc
ASTM D792
Water Absorption 0.10 %

@Time 86400 sec
 0.10 %

@Time 24.0 hour
 ASTM D570
Linear Mold Shrinkage, Flow 0.0060 - 0.0090 cm/cm

@Thickness 3.20 mm
 0.0060 - 0.0090 in/in

@Thickness 0.126 in
 SABIC Method
Mechanical Properties Metric English Comments
Tensile Strength, Yield 63.0 MPa
9140 psi
SABIC - Japan Method
Elongation at Break 220 %
220 %
SABIC - Japan Method
Flexural Strength 84.0 MPa
12200 psi
ASTM D790
Flexural Modulus 2.13 GPa
309 ksi
ASTM D790
Izod Impact, Notched 7.35 J/cm
13.8 ft-lb/in
ASTM D256
Thermal Properties Metric English Comments
CTE, linear 60.0 - 80.0 µm/m-°C

@Temperature -30.0 - 30.0 °C
 33.3 - 44.4 µin/in-°F

@Temperature -22.0 - 86.0 °F
 TMA
Deflection Temperature at 0.46 MPa (66 psi) 120 °C

@Thickness 3.20 mm
 248 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Flammability, UL94 HB

@Thickness 1.40 mm
 HB

@Thickness 0.0551 in
 UL 94
Electrical Properties Metric English Comments
Surface Resistance 1.00e+16 ohm
1.00e+16 ohm
ASTM D257
Dielectric Constant 3.2

@Frequency 50.0 - 60.0 Hz
 3.2

@Frequency 50.0 - 60.0 Hz
 ASTM D150