LG Chemical Lupox® SG3250M PBT+PET+MF25%
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , PBT + PET, Mineral Filled , Polyethylene Terephthalate (PET) |
| Manufacturer | LG Chemical |
| Trade Name | Lupox® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical Lupox® SG3250M PBT+PET+MF25%.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Injection Molding, PBT+PET+MF25%, Good SurfaceApplication: Automotive (Head Lamp Bezel)CAS No. 24968-12-5, 25038-59-9 and 14807-96-6Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.54 g/cc | 1.54 g/cc | ASTM D792 |
| Maximum Moisture Content | 0.020 | 0.020 | Injection Molding |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.012 cm/cm @Thickness 3.20 mm |
0.0050 - 0.012 in/in @Thickness 0.126 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 44.1 MPa @Thickness 3.20 mm |
6400 psi @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Elongation at Break | 3.5 % @Thickness 3.20 mm |
3.5 % @Thickness 0.126 in |
5mm/min; ASTM D638 |
| Flexural Yield Strength | 83.4 MPa @Thickness 3.20 mm |
12100 psi @Thickness 0.126 in |
1.3mm/min; ASTM D790 |
| Flexural Modulus | 4.31 GPa @Thickness 3.20 mm |
626 ksi @Thickness 0.126 in |
1.3mm/min; ASTM D790 |
| Izod Impact, Notched | 0.294 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
0.551 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 225 °C | 437 °F | @ Break; ASTM D3418 |
| Deflection Temperature at 0.46 MPa (66 psi) | 200 °C @Thickness 6.40 mm |
392 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 245 - 255 °C | 473 - 491 °F | Injection Molding |
| Middle Barrel Temperature | 250 - 260 °C | 482 - 500 °F | Injection Molding |
| Front Barrel Temperature | 255 - 265 °C | 491 - 509 °F | Injection Molding |
| Nozzle Temperature | 255 - 265 °C | 491 - 509 °F | Injection Molding |
| Melt Temperature | 255 - 265 °C | 491 - 509 °F | Injection Molding |
| Mold Temperature | 80.0 - 100 °C | 176 - 212 °F | Injection Molding |
| Drying Temperature | 120 °C | 248 °F | Injection Molding |
| Dry Time | 4.00 - 5.00 hour | 4.00 - 5.00 hour | Injection Molding |
Users viewing this material also viewed the following:
- Premix Thermoplastics PRE-ELEC® PP 1380
- Polykemi AB POLYfill PP EQX10030R UV Polypropylene, Mineral Reinforced, Modified
- Pyrotek MC-1 Metal Ceramic Thermocouple Protection Tube
- Indium Corp. Indalloy 104 Tin-Lead Solder Alloy
- Solvay Specialty Polymers AvaSpire® AV-650 GF30 Polyaryletherketone (PAEK), 30% Glass Fiber
- Sinotek Materials Packing Carbon Fiber with Graphite
- SABIC Innovative Plastics LNP Thermocomp ZF-1006 BK8-950 PPE+PS
- DSM Arnite® BM4 240 (PBT+PET)-MD20
- 3M Scotch® 8621 Tear Strip Tape
- 3M Scotch® 828 Custom Printed Pouch Tape
Copyright © lookpolymers.com All Rights Reserved