Azoty Tarnow™ TARNOFORM 300 HI6 POM
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Impact Modified |
| Manufacturer | Azoty Tarnow™ (Zaklady Azotowe) |
| Trade Name | TARNOFORM |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Azoty Tarnow™ TARNOFORM 300 HI6 POM.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Rubber modified grade with very high impact strength and damping capacity.Information provided by Zakłady Azotowe w Tarnowie-Moscicach S.A.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.33 g/cc | 0.0480 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.0265 cm/cm | 0.0265 in/in | |
| Melt Flow | 5.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
5.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 87 | 87 | ISO 2039-2 |
| Ball Indentation Hardness | 52.0 MPa | 7540 psi | 132 N; ISO 2039-1 |
| Tensile Strength, Yield | 32.0 MPa | 4640 psi | ISO 527 |
| Elongation at Break | 180 % | 180 % | ISO 527 |
| Flexural Strength | 27.0 MPa | 3920 psi | ISO 178 |
| Izod Impact, Notched (ISO) | 17.0 kJ/m² | 8.09 ft-lb/in² | 1A; ISO 180 |
| Charpy Impact, Notched | 1.80 J/cm² | 8.57 ft-lb/in² | 1eA; ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Heat Capacity | 1.48 J/g-°C | 0.354 BTU/lb-°F | |
| Melting Point | 167 °C | 333 °F | 10°C/min.; ISO 3146 |
| Deflection Temperature at 1.8 MPa (264 psi) | 67.0 °C | 153 °F | ISO 75 |
| Vicat Softening Point | 99.0 °C | 210 °F | 50 N; ISO 306 |
| Flammability, UL94 | HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | IEC 60093 |
| Dielectric Constant | 4.5 @Frequency 1e+6 Hz |
4.5 @Frequency 1e+6 Hz |
IEC 60250 |
| Dielectric Strength | 20.0 kV/mm | 508 kV/in | IEC 60243 |
| Dissipation Factor | 0.0425 @Frequency 1e+6 Hz |
0.0425 @Frequency 1e+6 Hz |
IEC 60250 |
| Comparative Tracking Index | 600 V | 600 V | IEC 112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 180 - 210 °C | 356 - 410 °F | Barrel temperature |
| Mold Temperature | 50.0 - 80.0 °C | 122 - 176 °F |
Users viewing this material also viewed the following:
- Plastcom SLOVALEN PC 16 FRD 1 PP, flame retardant
- LyondellBasell Petrothene® LP500200 High Density Polyethylene (Sheet & Profile Grade)
- Techmer ES Electrablend® ABS CF20 BK 20% Carbon Filled
- Shakespeare S-3 Economy Nylon Copolymer Fishing Line, 200 lb
- A. Schulman POLYFORT™ FXP 2779U UV Stabilized Copolymer Polypropylene
- Excalibar NewBar™ API Barite BaSO4 Powder
- 3M FVS15S Static Cling Label Materials
- BASF Polystyrol® 158 K Polystyrene (Global)
- Parylene Coating Services D Poly (P-Xylylene)
Copyright © lookpolymers.com All Rights Reserved