- Eurostar Staramide PF007IX2 PA6, Glass Fiber Filled, Impact Modified, Injection Molded
Eurostar Staramide PF007IX2 PA6, Glass Fiber Filled, Impact Modified, Injection Molded
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Glass Filled, Impact Grade |
| Manufacturer | Eurostar Engineering Plastics |
| Trade Name | Staramide |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eurostar Staramide PF007IX2 PA6, Glass Fiber Filled, Impact Modified, Injection Molded.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Staramide PF007IX1 is an Impact Modified, Glass Fiber Reinforced, Polyamide 6 Injection Molding Resin (also known as Star X 2010 33V)Information provided by Eurostar.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.36 g/cc | 0.0491 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm @Thickness 4.00 mm |
0.0020 in/in @Thickness 0.157 in |
E2P method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 123 MPa | 17800 psi | 5 mm/min; ISO 527 |
| Tensile Strength, Yield | 125 MPa | 18100 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 3.0 % | 3.0 % | 5 mm/min; ISO 527 |
| 4.0 % | 4.0 % | Flexural, 2 mm/min; ISO 178 | |
| Elongation at Yield | 2.9 % | 2.9 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 8.70 GPa | 1260 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 171 MPa | 24800 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 6.80 GPa | 986 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 50.0 kJ/m² | 23.8 ft-lb/in² | 80x10x4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 55.0 kJ/m² | 26.2 ft-lb/in² | 80x10x4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 27.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
15.0 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 122 µm/m-°C @Temperature 23.0 - 60.0 °C |
67.8 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 217 °C | 423 °F | Flatw 80x10x4, sp=64 mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | Flatw 80x10x4, sp=64 mm; ISO 75/Af |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Zone 1 | 240 - 250 °C | 464 - 482 °F | |
| Zone 2 | 250 - 260 °C | 482 - 500 °F | |
| Zone 3 | 250 - 260 °C | 482 - 500 °F | |
| Melt Temperature | 250 - 260 °C | 482 - 500 °F | |
| Mold Temperature | 50.0 - 90.0 °C | 122 - 194 °F | |
| Drying Temperature | 80.0 °C @Time 14400 sec |
176 °F @Time 4.00 hour |
|
| Moisture Content | 0.20 % | 0.20 % |
Users viewing this material also viewed the following:
- Honeywell Capran® Emblem™ 1200Matte Matte Coated Bi-Axially Oriented Nylon Film
- LATI Latilub 80-10T K/15 PPS, 15% Carbon Fiber Reinforced, PTFE Filled
- SABIC Innovative Plastics LNP LUBRICOMP IBP34 PA6.12
- SABIC Innovative Plastics ULTEM 4000 PEI (Asia Pacific)
- Techmer ES HiFill® PA6 E U
- SABIC Innovative Plastics NORYL PX1134 PPE+HIPS (Europe-Africa-Middle East)
- ArcelorMittal Complex Phase Steel 1000 Very high strength steel, Cold Rolled Steel
- DSM Akulon® F132-E Nylon 6 (European Grade) (Dry) (discontinued **)
- Special Metals INCOLOY® Alloy 020
Copyright © lookpolymers.com All Rights Reserved