- LG Chemical LUPOY GN-2151F Halogen Free Modified PC, 15% Glass Fiber Reinforced, Flame Retardant, Green
LG Chemical LUPOY GN-2151F Halogen Free Modified PC, 15% Glass Fiber Reinforced, Flame Retardant, Green
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Glass Fiber Filled, Flame Retardant |
| Manufacturer | LG Chemical |
| Trade Name | LUPOY |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical LUPOY GN-2151F Halogen Free Modified PC, 15% Glass Fiber Reinforced, Flame Retardant, Green.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Among the characteristics of LUPOY polycarbonate resins are excellent mechanical properties, high heat resistance, high impact strength, and dimensional stability.Applications:Automotive: Automotive front ends, cluster pad main panel (instrument panel), lower cluster pad main, console box, glove box cover, door, wheel cover and cap, defroster grill, back mirror housingElectrical and Electronic: Monitor housing, fax housing, notebook PC housing, cellular phone case, fax and copy machine frame, CD ROM drive tray and main frame, relay case, connector, switchIndustrial Parts and Household Appliance: Helmet, terminal box, electrical tool housing, industrial bobbin, distributing board box, power tool component, gears and cams, water meter housingInformation Provided by LG Chem
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.30 g/cc | 1.30 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0040 cm/cm | 0.0040 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 124 | 124 | ASTM D785 |
| Tensile Strength, Yield | 83.0 MPa | 12000 psi | ASTM D638 |
| Elongation at Break | 9.0 % | 9.0 % | ASTM D638 |
| Flexural Strength | 140 MPa | 20300 psi | ASTM D790 |
| Flexural Modulus | 4.655 GPa | 675.2 ksi | ASTM D790 |
| Izod Impact, Notched | 0.980 J/cm @Temperature 23.0 °C |
1.84 ft-lb/in @Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 143 °C | 289 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 270 - 300 °C | 518 - 572 °F | |
| Middle Barrel Temperature | 280 - 315 °C | 536 - 599 °F | |
| Front Barrel Temperature | 290 - 330 °C | 554 - 626 °F | |
| Nozzle Temperature | 290 - 330 °C | 554 - 626 °F | |
| Melt Temperature | 300 - 340 °C | 572 - 644 °F | |
| Mold Temperature | 80.0 - 115 °C | 176 - 239 °F | |
| Drying Temperature | 100 - 120 °C | 212 - 248 °F | |
| Dry Time | 3 - 5 hour | 3 - 5 hour | |
| Screw Speed | 40 - 70 rpm | 40 - 70 rpm |
Users viewing this material also viewed the following:
- Ravago Manufacturing Americas Hylon® N1033STL Nylon 6/6 (DAM)
- Phillips 66 COPYLENE® CH110 Polypropylene, Homopolymer, BCF
- MarkeTech Neodymium Gallium Oxide (NdGaO3) Single Crystal Substrate
- Techmer ES HiFill® PES GF20 TL15 LE 20% Glass Filled
- A. Schulman PAPERMATCH® T-4228-50 Specialty Masterbatch
- A. Schulman POLYAXIS® RLLP621 Flame Retardant, High Density Polyethylene
- A. Schulman POLYBATCH™ Red 5500 Concentrate Based In Polyethylene
- Dow Corning 786 SILICONE MILDEW RESISTANT SEALANT
Copyright © lookpolymers.com All Rights Reserved