LG Chemical LUCON PN9008 PPS+MF+GF

Category	Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) , Polyphenylene Sulfide (PPS), Mineral/Glass-Fiber Filled
Manufacturer	LG Chemical
Trade Name	LUCON
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	LG Chemical LUCON PN9008 PPS+MF+GF.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Injection Molding Grade, PPS+MF+GF, High Thermal Conductivity, Chemical Resistance, High Heat ResistanceApplication: Electrical or Electronic Parts (Heat sink, LED etc.), Motor HousingsCAS No. 25212-74-2, 409-21-2 and 65997-17-3Information provided by LG Chemical

Physical Properties	Metric	English	Comments
Specific Gravity	1.95 g/cc	1.95 g/cc	ASTM D792
Maximum Moisture Content	0.010	0.010	Injection Molding
Linear Mold Shrinkage, Flow	0.0040 - 0.010 cm/cm @Thickness 3.20 mm	0.0040 - 0.010 in/in @Thickness 0.126 in	ASTM D955

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	73.5 MPa @Thickness 3.20 mm	10700 psi @Thickness 0.126 in	5mm/min; ASTM D638
Elongation at Break	>= 5.0 % @Thickness 3.20 mm	>= 5.0 % @Thickness 0.126 in	5mm/min; ASTM D638
Flexural Yield Strength	127 MPa @Thickness 6.40 mm	18500 psi @Thickness 0.252 in	1mm/min; ASTM D790
Flexural Modulus	12.9 GPa @Thickness 6.40 mm	1880 ksi @Thickness 0.252 in	1mm/min; ASTM D790
Izod Impact, Notched	0.196 J/cm @Thickness 3.20 mm, Temperature 23.0 Â°C	0.367 ft-lb/in @Thickness 0.126 in, Temperature 73.4 Â°F	ASTM D256

Thermal Properties	Metric	English	Comments
Thermal Conductivity	1.70 W/m-K	11.8 BTU-in/hr-ftÂ²-Â°F	Laser flash method
Deflection Temperature at 0.46 MPa (66 psi)	250 Â°C @Thickness 6.40 mm	482 Â°F @Thickness 0.252 in	ASTM D648
Flammability, UL94	V-0 @Thickness >=0.800 mm	V-0 @Thickness >=0.0315 in
	V-0 @Thickness >=1.60 mm	V-0 @Thickness >=0.0630 in
	V-0 @Thickness >=2.50 mm	V-0 @Thickness >=0.0984 in
	V-0 @Thickness >=3.20 mm	V-0 @Thickness >=0.126 in

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+16 ohm-cm	1.00e+16 ohm-cm	ASTM D257
Surface Resistance	1.00e+16 ohm	1.00e+16 ohm	IEC 60093

Processing Properties	Metric	English	Comments
Rear Barrel Temperature	280 - 310 Â°C	536 - 590 Â°F	Injection Molding
Middle Barrel Temperature	310 - 320 Â°C	590 - 608 Â°F	Injection Molding
Front Barrel Temperature	320 - 325 Â°C	608 - 617 Â°F	Injection Molding
Nozzle Temperature	310 - 330 Â°C	590 - 626 Â°F	Injection Molding
Melt Temperature	330 Â°C	626 Â°F	Resin, Injection Molding
Mold Temperature	130 - 150 Â°C	266 - 302 Â°F	Injection Molding
Drying Temperature	120 - 140 Â°C	248 - 284 Â°F	Injection Molding
Dry Time	3.00 - 5.00 hour	3.00 - 5.00 hour	Injection Molding
Back Pressure	0.981 - 3.92 MPa	142 - 569 psi	Injection Molding
Screw Speed	40 - 80 rpm	40 - 80 rpm	Injection Molding