LG Chemical LUCON CP-4208F Conductive Thermoplastic, Flame Retardant

Category Polymer , Thermoplastic
Manufacturer LG Chemical
Trade Name LUCON
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LG Chemical LUCON CP-4208F Conductive Thermoplastic, Flame Retardant.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LG Chemicals has formulated a diverse range of LUCON thermoplastic compounds containing conductive additives, such as carbon powder, (nickel coated) carbon fiber, or stainless steel fiber for solving problems associated with build-up of electrostatic charges, electrostatic discharge, and electromagnetic interference. These materials span the surface resistivity spectrum from antistatic through conductive to EMI shielding (100-1012O).Applications: I.C. tray, wafer carrier, I.C. magazine, notebook PC case, home appliance part, LCD cassette trayInformation Provided by LG Chem
Physical Properties Metric English Comments
Specific Gravity 1.25 g/cc
1.25 g/cc
ASTM D792
Linear Mold Shrinkage 0.0010 cm/cm
0.0010 in/in
ASTM D955
Mechanical Properties Metric English Comments
Hardness, Rockwell M 95
95
ASTM D785
Tensile Strength at Break 142 MPa
20600 psi
ASTM D638
Elongation at Break <= 10 %
<= 10 %
ASTM D638
Flexural Strength 196 MPa
28400 psi
ASTM D790
Flexural Modulus 9.81 GPa
1420 ksi
ASTM D790
Izod Impact, Notched 0.490 J/cm
0.918 ft-lb/in
ASTM D256
Thermal Properties Metric English Comments
Thermal Conductivity >= 0.270 W/m-K
>= 1.87 BTU-in/hr-ft²-°F
ASTM C177
Deflection Temperature at 1.8 MPa (264 psi) 95.0 °C
203 °F
ASTM D648
Electrical Properties Metric English Comments
Volume Resistivity 10000 ohm-cm - 1e+05
10000 ohm-cm - 1e+05
ASTM D257
Surface Resistance 10000 ohm - 1e+05
10000 ohm - 1e+05
ASTM D257
Processing Properties Metric English Comments
Rear Barrel Temperature 260 - 300 °C
500 - 572 °F
Middle Barrel Temperature 270 - 320 °C
518 - 608 °F
Front Barrel Temperature 275 - 320 °C
527 - 608 °F
Nozzle Temperature 275 - 320 °C
527 - 608 °F
Melt Temperature 280 - 320 °C
536 - 608 °F
Mold Temperature 80.0 - 120 °C
176 - 248 °F
Drying Temperature 120 °C
248 °F
Dry Time 4 hour
4 hour
Injection Pressure 49.03 - 78.45 MPa
7111 - 11380 psi
Second
68.65 - 88.26 MPa
9957 - 12800 psi
First
Back Pressure 0.000 - 1.96 MPa
0.000 - 284 psi
Screw Speed 40 - 60 rpm
40 - 60 rpm