LG Chemical LG713 ABS, Low Gloss

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Molded
Manufacturer LG Chemical
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LG Chemical LG713 ABS, Low Gloss.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Feature: Extrusion Molding, Low Gloss, ExtrusionApplication: Automotive Interior Housing (Cover Etc)CAS No. 25120-20-1, 9003-56-9 and 31621-07-5Information provided by LG Chemical
Physical Properties Metric English Comments
Specific Gravity 1.04 g/cc
1.04 g/cc
ASTM D792
Maximum Moisture Content 0.010
0.010
Extrusion Molding
Linear Mold Shrinkage, Flow 0.0040 - 0.0070 cm/cm

@Thickness 3.20 mm
 0.0040 - 0.0070 in/in

@Thickness 0.126 in
 ASTM D955
Melt Flow 4.0 g/10 min

@Load 10.0 kg,
Temperature 220 °C
 4.0 g/10 min

@Load 22.0 lb,
Temperature 428 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 96
96
ASTM D785
Tensile Strength, Yield 37.3 MPa

@Thickness 3.20 mm
 5400 psi

@Thickness 0.126 in
 50 mm/min; ASTM D638
Elongation at Break 40 %

@Thickness 3.20 mm
 40 %

@Thickness 0.126 in
 50 mm/min; ASTM D638
Flexural Yield Strength 60.8 MPa

@Thickness 3.20 mm
 8820 psi

@Thickness 0.126 in
 15 mm/min; ASTM D790
Flexural Modulus 1.92 GPa

@Thickness 3.20 mm
 279 ksi

@Thickness 0.126 in
 15 mm/min; ASTM D790
Izod Impact, Notched 2.26 J/cm

@Thickness 6.40 mm,
Temperature 23.0 °C
 4.22 ft-lb/in

@Thickness 0.252 in,
Temperature 73.4 °F
 ASTM D256
2.55 J/cm

@Thickness 3.20 mm,
Temperature 23.0 °C
 4.78 ft-lb/in

@Thickness 0.126 in,
Temperature 73.4 °F
 ASTM D256
Izod Impact, Unnotched 1.08 J/cm

@Thickness 6.40 mm,
Temperature -30.0 °C
 2.02 ft-lb/in

@Thickness 0.252 in,
Temperature -22.0 °F
 ASTM D256
1.18 J/cm

@Thickness 3.20 mm,
Temperature -30.0 °C
 2.20 ft-lb/in

@Thickness 0.126 in,
Temperature -22.0 °F
 ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 97.0 °C

@Thickness 6.40 mm
 207 °F

@Thickness 0.252 in
 Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 90.0 °C

@Thickness 6.40 mm
 194 °F

@Thickness 0.252 in
 Unannealed; ASTM D648
Vicat Softening Point 95.0 °C

@Load 5.00 kg
 203 °F

@Load 11.0 lb
 50°C/h; ASTM D1525
Optical Properties Metric English Comments
Gloss 30 %
30 %
45°; ASTM D2457
Processing Properties Metric English Comments
Zone 1 180 - 210 °C
356 - 410 °F
Extrusion Molding
Zone 2 190 - 230 °C
374 - 446 °F
Extrusion Molding
Zone 3 200 - 250 °C
392 - 482 °F
Extrusion Molding
Zone 4 200 - 250 °C
392 - 482 °F
Extrusion Molding
Adapter Temperature 200 - 250 °C
392 - 482 °F
Extrusion Molding
Die Temperature 200 - 250 °C
392 - 482 °F
Extrusion Molding
Melt Temperature 200 - 250 °C
392 - 482 °F
Extrusion Molding
Roll Temperature 60.0 - 90.0 °C
140 - 194 °F
Bottom, Extrusion
70.0 - 90.0 °C
158 - 194 °F
Middle, Extrusion
70.0 - 100 °C
158 - 212 °F
Top, Extrusion
Drying Temperature 70.0 - 80.0 °C
158 - 176 °F
Extrusion Molding
Dry Time 3.00 - 4.00 hour
3.00 - 4.00 hour
Extrusion Molding