LG Chemical LG-703A ABS, Low Gloss, General Purpose
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Molded |
| Manufacturer | LG Chemical |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical LG-703A ABS, Low Gloss, General Purpose.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information Provided by LG Chem
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in³ | ISO 1183 |
| Water Absorption | 0.30 % | 0.30 % | ISO 62 |
| Linear Mold Shrinkage | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | ISO 2577 |
| Melt Index of Compound | 5.67 g/10 min @Load 10.0 kg, Temperature 220 °C |
5.67 g/10 min @Load 22.0 lb, Temperature 428 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 45.0 MPa | 6530 psi | 50 mm/min; ISO 527 |
| Elongation at Break | 20 % | 20 % | 50 mm/min; ISO 527 |
| Elongation at Yield | 5.0 % | 5.0 % | 50 mm/min; ISO 527 |
| Tensile Modulus | 2.25 GPa | 326 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 77.0 MPa | 11200 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 2.50 GPa | 363 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 8.00 kJ/m² @Temperature -30.0 °C |
3.81 ft-lb/in² @Temperature -22.0 °F |
ISO 180 |
| 15.0 kJ/m² @Temperature 23.0 °C |
7.14 ft-lb/in² @Temperature 73.4 °F |
ISO 80 | |
| Charpy Impact Unnotched | 5.00 J/cm² @Temperature -30.0 °C |
23.8 ft-lb/in² @Temperature -22.0 °F |
ISO 179 |
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ISO 179 | |
| Charpy Impact, Notched | 0.900 J/cm² @Temperature -30.0 °C |
4.28 ft-lb/in² @Temperature -22.0 °F |
ISO 179 |
| 1.80 J/cm² @Temperature 23.0 °C |
8.57 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 80.0 µm/m-°C @Temperature 20.0 °C |
44.4 µin/in-°F @Temperature 68.0 °F |
ISO 11359 |
| CTE, linear, Transverse to Flow | 92.0 µm/m-°C @Temperature 20.0 °C |
51.1 µin/in-°F @Temperature 68.0 °F |
ISO 11359 |
| Deflection Temperature at 0.46 MPa (66 psi) | 106 °C | 223 °F | Annealed, 80°C, 4 hours; ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 101 °C | 214 °F | Annealed, 80°C, 4 hours; ISO 175 |
| Vicat Softening Point | 102 °C | 216 °F | 50 N, 50°C/h; ISO 306 |
| Flammability, UL94 | HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
|
| HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 220 - 250 °C | 428 - 482 °F | |
| Mold Temperature | 40.0 - 80.0 °C | 104 - 176 °F | |
| Drying Temperature | 75.0 - 85.0 °C | 167 - 185 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | Predrying |
Users viewing this material also viewed the following:
- Solvay Specialty Polymers Cogegum® AFR/765 Polyolefin
- SABIC Innovative Plastics LNP Thermocomp WC003P Polyester Elastomer
- Shin-Etsu Silicones KE-3494 Silicone, RTV
- A. Schulman POLYFORT™ FPP 1606 Glass Filled Chemically Coupled Impact Copolymer Polypropylene
- EMS-Griltech Griltex® D 1541A Copolyamide Hotmelt Adhesive (Apparel Interlinings)
- Aclo Accutech ABS ABS831G30L Glass Reinforced
- Abatron AboCast 8503-5/AboCure 8503-5 Colorless Epoxy
- Caplinq LINQSTAT™ VCF-40012T/2
- ArcelorMittal HSLA 380 High strength low alloy steel for cold forming, Cold Rolled
- Colorite Polymers 2019F Rigid PVC
Copyright © lookpolymers.com All Rights Reserved