LG Chemical KEYFLEX BT GN7155F Ester Type TPE
| Category | Polymer , Thermoplastic , Elastomer, TPE , Polyester, TP , Polyester Thermoplastic Elastomer |
| Manufacturer | LG Chemical |
| Trade Name | KEYFLEX |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical KEYFLEX BT GN7155F Ester Type TPE.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Extrusion Molding, TPC-ET, Halogen Free Flame Retardant, Medium ModulusApplication: Cable & Wire Jackets, Hose & Tubing, SheetInformation provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.23 g/cc | 1.23 g/cc | ASTM D792 |
| Maximum Moisture Content | 0.010 | 0.010 | Injection Molding |
| 0.010 | 0.010 | Extrusion Molding | |
| Melt Flow | 10 g/10 min @Load 2.16 kg, Temperature 230 °C |
10 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 56 | 56 | ASTM D2240 |
| Tensile Strength at Break | 22.6 MPa @Thickness 2.00 mm |
3280 psi @Thickness 0.0787 in |
50mm/min; ASTM D638 |
| Elongation at Break | 250 % @Thickness 2.00 mm |
250 % @Thickness 0.0787 in |
50mm/min; ASTM D638 |
| Flexural Modulus | 0.245 GPa @Thickness 6.40 mm |
35.6 ksi @Thickness 0.252 in |
15mm/min; ASTM D790 |
| Izod Impact, Notched | 1.47 J/cm @Thickness 6.40 mm, Temperature 23.0 °C |
2.76 ft-lb/in @Thickness 0.252 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 200 °C | 392 °F | Peak |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Strength | 24.0 kV/mm @Thickness 1.00 mm |
610 kV/in @Thickness 0.0394 in |
ASTM D149 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 200 - 220 °C | 392 - 428 °F | Injection Molding |
| Middle Barrel Temperature | 210 - 230 °C | 410 - 446 °F | Injection Molding |
| Front Barrel Temperature | 220 - 240 °C | 428 - 464 °F | Injection Molding |
| Nozzle Temperature | 220 - 240 °C | 428 - 464 °F | Injection Molding |
| Zone 1 | 200 - 220 °C | 392 - 428 °F | Extrusion Molding |
| Zone 2 | 210 - 230 °C | 410 - 446 °F | Extrusion Molding |
| Zone 3 | 215 - 235 °C | 419 - 455 °F | Extrusion Molding |
| Zone 4 | 220 - 240 °C | 428 - 464 °F | Extrusion Molding |
| Adapter Temperature | 220 - 240 °C | 428 - 464 °F | Extrusion Molding |
| Die Temperature | 210 - 250 °C | 410 - 482 °F | Extrusion Molding |
| Melt Temperature | 200 - 240 °C | 392 - 464 °F | Injection Molding |
| 200 - 240 °C | 392 - 464 °F | Extrusion Molding | |
| Mold Temperature | 40.0 - 60.0 °C | 104 - 140 °F | Injection Molding |
| Drying Temperature | 80.0 - 90.0 °C | 176 - 194 °F | Injection Molding |
| 80.0 - 90.0 °C | 176 - 194 °F | Extrusion Molding | |
| Dry Time | 3.00 - 4.00 hour | 3.00 - 4.00 hour | Injection Molding |
| 3.00 - 4.00 hour | 3.00 - 4.00 hour | Extrusion Molding |
Users viewing this material also viewed the following:
- Reliance Industries Reclair F22020 Polyethylene
- SABIC Innovative Plastics Lexan® LS3 PC (Asia Pacific)
- ExxonMobil Exceed™ 399L60 LDPE/Hexene Premium Blown Film Resin, 0.8 mil Film (discontinued **)
- DuPont Performance Polymers Zytel® 101 NC010 Nylon 66 (Unverified Data**)
- Plastics Group Polifil® RP-LDPE Low Density Polyethylene
- ELASTO UK Mediprene™ 660420M TPE, Medical Applications, 42A Hardness
- Dow ELITE™ 5220G Enhanced Polyethylene Resin
- ATI Allegheny Ludlum Stainless Steel Chromium-Nickel-Manganese AL 201LN™, M-6 (UNS S20153)
Copyright © lookpolymers.com All Rights Reserved