LATI Latilub 87/28-20T PC, PTFE Filled

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, PTFE Filled
Manufacturer LATI
Trade Name Latilub
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Latilub 87/28-20T PC, PTFE Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Self-lubricating product based on Polycarbonate (PC). PTFE.Information provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.32 g/cc
0.0477 lb/in³
Linear Mold Shrinkage, Flow 0.0055 - 0.0075 cm/cm
0.0055 - 0.0075 in/in
Linear Mold Shrinkage, Transverse 0.0060 - 0.0075 cm/cm
0.0060 - 0.0075 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 55.0 MPa
7980 psi
Elongation at Break 8.0 %
8.0 %
Elongation at Yield 3.0 %
3.0 %
Tensile Modulus 2.20 GPa
319 ksi
Charpy Impact Unnotched 5.00 J/cm²
23.8 ft-lb/in²
Charpy Impact, Notched 1.20 J/cm²
5.71 ft-lb/in²
Coefficient of Friction, Dynamic 0.14
0.14
Coefficient of Friction, Static 0.18
0.18
K (wear) Factor 3.50 x 10-8 mm³/N-M
1.74 x 10-10 in³-min/ft-lb-hr
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 140 °C
284 °F
Deflection Temperature at 1.8 MPa (264 psi) 130 °C
266 °F
Vicat Softening Point 145 °C

@Load 5.00 kg
 293 °F

@Load 11.0 lb
Flammability, UL94 HB

@Thickness 1.50 mm
 HB

@Thickness 0.0591 in
V-1

@Thickness 3.00 mm
 V-1

@Thickness 0.118 in
Processing Properties Metric English Comments
Melt Temperature 265 - 300 °C
509 - 572 °F
Mold Temperature 80.0 - 100 °C
176 - 212 °F
Drying Temperature 110 - 130 °C

@Time 10800 sec
 230 - 266 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa
Users viewing this material also viewed the following: