LATI Latilub 80-40GRT PPS, Graphite/PTFE Filled

Category	Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) , Polyphenylene Sulfide (PPS) with PTFE Filler
Manufacturer	LATI
Trade Name	Latilub
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	LATI Latilub 80-40GRT PPS, Graphite/PTFE Filled.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Self-lubricating product based on Polyphenylene Sulfide (PPS). Graphite / PTFE. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.

Physical Properties	Metric	English
Density	1.60 g/cc	0.0578 lb/inÂ³
Linear Mold Shrinkage, Flow	0.0045 - 0.0075 cm/cm	0.0045 - 0.0075 in/in
Linear Mold Shrinkage, Transverse	0.0050 - 0.0080 cm/cm	0.0050 - 0.0080 in/in

Mechanical Properties	Metric	English
Tensile Strength at Break	50.0 MPa	7250 psi
Elongation at Break	1.0 %	1.0 %
Tensile Modulus	6.80 GPa	986 ksi
Charpy Impact Unnotched	1.00 J/cmÂ²	4.76 ft-lb/inÂ²
Charpy Impact, Notched	0.150 J/cmÂ²	0.714 ft-lb/inÂ²
Coefficient of Friction, Dynamic	0.090	0.090
Coefficient of Friction, Static	0.16	0.16
K (wear) Factor	4.70 x 10^-8 mmÂ³/N-M	2.33 x 10^-10 inÂ³-min/ft-lb-hr

Thermal Properties	Metric	English
Deflection Temperature at 0.46 MPa (66 psi)	250 Â°C	482 Â°F
Deflection Temperature at 1.8 MPa (264 psi)	150 Â°C	302 Â°F
Vicat Softening Point	245 Â°C @Load 5.00 kg	473 Â°F @Load 11.0 lb

Processing Properties	Metric	English
Melt Temperature	290 - 310 Â°C	554 - 590 Â°F
Mold Temperature	130 - 150 Â°C	266 - 302 Â°F
Drying Temperature	130 - 150 Â°C @Time 10800 sec	266 - 302 Â°F @Time 3.00 hour

Descriptive Properties	Value	Comments
ISO Shrinkage - Pressure	60 MPa