LATI Latilub 66-20T G/20-V1 PA66, 20% Glass Fiber Reinforced, PTFE Filled, Flame Retardant
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Glass Fiber Filled, Flame Retardant , Nylon 66, Glass Fiber/PTFE Filled |
| Manufacturer | LATI |
| Trade Name | Latilub |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LATI Latilub 66-20T G/20-V1 PA66, 20% Glass Fiber Reinforced, PTFE Filled, Flame Retardant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Self-lubricating product based on Polyamide 66 (PA66). PTFE. Glass fibers. UL94 V-1 classified, with brominated flame retardants, PBB/PBDE free.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.46 g/cc | 0.0527 lb/in³ | |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0065 cm/cm | 0.0050 - 0.0065 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0090 - 0.012 cm/cm | 0.0090 - 0.012 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 115 MPa | 16700 psi | |
| Elongation at Break | 2.5 % | 2.5 % | |
| Tensile Modulus | 6.40 GPa | 928 ksi | |
| Charpy Impact Unnotched | 3.50 J/cm² | 16.7 ft-lb/in² | |
| Charpy Impact, Notched | 0.800 J/cm² | 3.81 ft-lb/in² | |
| Coefficient of Friction, Dynamic | 0.24 | 0.24 | |
| Coefficient of Friction, Static | 0.30 | 0.30 | |
| K (wear) Factor | 6.20 x 10-8 mm³/N-M | 3.08 x 10-10 in³-min/ft-lb-hr |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 265 °C | 509 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | |
| Vicat Softening Point | 250 °C @Load 5.00 kg |
482 °F @Load 11.0 lb |
|
| Flammability, UL94 | V-1 @Thickness 3.00 mm |
V-1 @Thickness 0.118 in |
|
| V-1 @Thickness 1.50 mm |
V-1 @Thickness 0.0591 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 270 - 290 °C | 518 - 554 °F | |
| Mold Temperature | 70.0 - 100 °C | 158 - 212 °F | |
| Drying Temperature | 90.0 - 100 °C @Time 10800 sec |
194 - 212 °F @Time 3.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| ISO Shrinkage - Pressure | 60 MPa |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Wire & Cable 1741-xx06D Polyvinyl Chloride, Flexible (PVC, Flexible)
- SABIC PVC 67S Suspension Polyvinyl Chloride for Rigid Extruded Products
- LyondellBasell Alathon® H5112 High Density Polyethylene, Injection Molding Grade
- Toyobo PELPRENE™ S2002 Polyester TPE, Ultra Heat-resistant
- ThyssenKrupp COR-TEN B Structural Steel
- DSM Stanyl® TW200F8 Nylon 46-40% Glass Reinforced (European Grade) (Dry)
- ACC QSil 40 QSI Quantum Silicones 40 Durometer Condensation Cure for Potting
- Styrolution NAS® 21 Acrylic Copolymer
Copyright © lookpolymers.com All Rights Reserved