LG Chemical LUTENE FB3000 LDPE Extrusion of Blown Film
| Category | Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Film Grade |
| Manufacturer | LG Chemical |
| Trade Name | LUTENE |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical LUTENE FB3000 LDPE Extrusion of Blown Film.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: LUTENE FB3000 is mainly intended for the extrusion of blown film with high mechanical property for the clarity bags in all thickness. LUTENE FB3000 have high mechanical property and enables the product of very thin, clear gloss film. (LUTENE FB3000 contains slip agent and antiblock agent.)Main Application: Clarity bags in all thickness, film for automatic packing, packing textiles, lightweight carrier bags, shrink film for packing, film for lamination.CAS No. 9002-88-4Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.921 g/cc | 0.921 g/cc | ASTM D1505 |
| Water Vapor Transmission | 10.5 g/m²/day | 0.676 g/100 in²/day | |
| Oxygen Transmission Rate | 2000 cc/m²/day | 129 cc/100 in²/day | |
| Nitrogen Transmission | 7500 cc-mm/m²-24hr-atm | 19100 cc-mil/100 in²-24hr-atm | |
| Melt Flow | 3.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
3.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Elongation at Break, MD | 420 % | 420 % | ASTM D882 |
| Film Elongation at Break, TD | 610 % | 610 % | ASTM D882 |
| Elmendorf Tear Strength MD | 8.83 g | 8.83 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 8.34 g | 8.34 g | ASTM D1922 |
| Dart Drop Test | 110 g | 0.243 lb | ASTM D1709 |
| Film Tensile Strength at Break, MD | 18.6 MPa | 2700 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 18.1 MPa | 2630 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 110 °C | 230 °F | DSC |
| Vicat Softening Point | 90.0 °C | 194 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 8.0 % | 8.0 % | ASTM D1003 |
| Gloss | 95 % | 95 % | 60°; ASTM D2457 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 140 - 160 °C | 284 - 320 °F | |
| Blow-up Ratio (BUR) | 1.5 - 3.0 | 1.5 - 3.0 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Slip Coefficient | 0.08 | ASMT D1894 |
Users viewing this material also viewed the following:
- Polimeri Europa KOBLEND HI 10 PBT+PC, Impact Grade (discontinued **)
- Momentive Performance Materials RTV88 Red Extreme High Temperature Potting/Encapsulating Compound
- SABIC Innovative Plastics XYLEX X7507 PC+POLYESTER (Europe-Africa-Middle East)
- Solvay MIRATAINE® BET CU Surfactant
- SABIC Innovative Plastics LNP VERTON RX89047 PA 66
- Zeon Chemicals HyTemp® NS-70 Polyacrylate Curative
- Arlon 51146R020 Silicone Rubber/Fiberglass Laminate
- Bulk Molding Compounds BMC 5209 Mineral Filled, Glass Reinforced Polyester
- Chosun Refractories TD-R75 Monolithic Refractories for Ladle and Tundish
Copyright © lookpolymers.com All Rights Reserved