BASF Polystyrol® 165 H Polystyrene (Europe)
| Category | Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Molded, Unreinforced |
| Manufacturer | BASF |
| Trade Name | Polystyrol® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Polystyrol® 165 H Polystyrene (Europe).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
High molecular grades, often blended with high-impact extrusion grades (e.g. for dairy products).Data was collected by ISO methods and provided by BASF.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in³ | |
| Water Absorption | 0.10 % | 0.10 % | |
| Moisture Absorption at Equilibrium | 0.10 % | 0.10 % | |
| Linear Mold Shrinkage, Flow | 0.0045 cm/cm | 0.0045 in/in | |
| Melt Flow | 2.5 g/10 min @Load 5.00 kg, Temperature 200 °C |
2.5 g/10 min @Load 11.0 lb, Temperature 392 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 52.0 MPa | 7540 psi | |
| Elongation at Break | 2.0 % | 2.0 % | |
| Tensile Modulus | 3.30 GPa | 479 ksi | |
| Charpy Impact Unnotched | 2.30 J/cm² | 10.9 ft-lb/in² | |
| Charpy Impact, Notched | 0.300 J/cm² | 1.43 ft-lb/in² | |
| Tensile Creep Modulus, 1 hour | 3300 MPa | 479000 psi | |
| Tensile Creep Modulus, 1000 hours | 2600 MPa | 377000 psi |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 80.0 µm/m-°C @Temperature 20.0 °C |
44.4 µin/in-°F @Temperature 68.0 °F |
|
| Deflection Temperature at 0.46 MPa (66 psi) | 84.0 °C | 183 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 76.0 °C | 169 °F | |
| Vicat Softening Point | 89.0 °C | 192 °F | |
| Glass Transition Temp, Tg | 90.0 °C | 194 °F | |
| Flammability, UL94 | HB @Thickness 3.18 mm |
HB @Thickness 0.125 in |
|
| Oxygen Index | 18 % | 18 % |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | |
| Dielectric Constant | 2.5 @Frequency 100 Hz |
2.5 @Frequency 100 Hz |
|
| 2.5 @Frequency 1e+6 Hz |
2.5 @Frequency 1e+6 Hz |
||
| Dissipation Factor | 0.000070 @Frequency 1e+6 Hz |
0.000070 @Frequency 1e+6 Hz |
|
| 0.000090 @Frequency 100 Hz |
0.000090 @Frequency 100 Hz |
||
| Comparative Tracking Index | 375 V | 375 V |
Users viewing this material also viewed the following:
- Multibase Multi-Flex® TPO D 4508 D 4508
- Outokumpu 4016 Ferritic Stainless Steel
- Polimeri Europa Clearflex® RM 50 U Linear Medium Density Polyethylene
- Momentive Performance Materials Siloprenâ„¢ LSR 2752 Liquid Silicone Rubber - Self-Bonding
- Zotefoams Evazote® VA65 Ethylene Vinyl Acetate Copolymer Foam
- CoorsTek SC-DSLP (SC-50) Liquid Phase Sintered Silicon Carbide
- Fainplast Compounds HAX HF 018/27F Halogen Free PVC
- CMT Materials HYTAC® LP Syntactic Plug Assist System for Heavy-Gauge Thermoforming
- Braskem LH218 Linear Low Density Polyethylene
- CENTROPLAST CENTROPHEN GF Polyphenylene ether 30% glass fiber
Copyright © lookpolymers.com All Rights Reserved