LATI Latigray 53/22-01 CX/70 PP Homopolymer, Impact Modified

Category	Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Impact Modified; Molded/Extruded
Manufacturer	LATI
Trade Name	Latigray
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	LATI Latigray 53/22-01 CX/70 PP Homopolymer, Impact Modified.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Radiopaque compound based on Polypropylene homopolymer (PPh), impact modified. Special mineral filler. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.

Physical Properties	Metric	English	Comments
Density	1.96 g/cc	0.0708 lb/inÂ³
Thickness	720 microns	28.3 mil	80
	840 microns	33.1 mil	120
Linear Mold Shrinkage, Flow	0.012 - 0.015 cm/cm	0.012 - 0.015 in/in
Linear Mold Shrinkage, Transverse	0.017 - 0.020 cm/cm	0.017 - 0.020 in/in

Mechanical Properties	Metric	English
Tensile Strength at Break	15.0 MPa	2180 psi
Elongation at Break	1.8 % @Temperature 23.0 Â°C	1.8 % @Temperature 73.4 Â°F
Elongation at Yield	0.90 % @Temperature 23.0 Â°C	0.90 % @Temperature 73.4 Â°F
Tensile Modulus	3.50 GPa	508 ksi
Charpy Impact Unnotched	3.00 J/cmÂ²	14.3 ft-lb/inÂ²
Charpy Impact, Notched	0.250 J/cmÂ²	1.19 ft-lb/inÂ²

Thermal Properties	Metric	English
Deflection Temperature at 0.46 MPa (66 psi)	130 Â°C	266 Â°F
Deflection Temperature at 1.8 MPa (264 psi)	110 Â°C	230 Â°F
Vicat Softening Point	120 Â°C @Load 5.00 kg	248 Â°F @Load 11.0 lb

Processing Properties	Metric	English
Melt Temperature	220 - 240 Â°C	428 - 464 Â°F
Mold Temperature	20.0 - 40.0 Â°C	68.0 - 104 Â°F
Drying Temperature	80.0 - 100 Â°C @Time 10800 sec	176 - 212 Â°F @Time 3.00 hour

Descriptive Properties	Value	Comments
ISO Shrinkage - Pressure	60 MPa