Entec Hypro™ PPC-GF40 Natural Impact Polypropylene, 40% Glass Reinforced
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 60% Glass Fiber Filler |
| Manufacturer | Entec Engineered Resins |
| Trade Name | Hypro™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Entec Hypro™ PPC-GF40 Natural Impact Polypropylene, 40% Glass Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Entec
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.22 g/cc | 0.0441 lb/in³ | ASTM D792 |
| Melt Flow | 10.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
10.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 86.0 MPa | 12500 psi | ASTM D638 |
| Elongation at Break | 3.00 % | 3.00 % | ASTM D638 |
| Elongation at Yield | 3.00 % | 3.00 % | ASTM D638 |
| Flexural Strength | 96.5 MPa | 14000 psi | ASTM D790 |
| Flexural Modulus | 4.828 GPa | 700.2 ksi | tangent; ASTM D790 |
| Izod Impact, Notched | 1.60 J/cm @Thickness 3.17 mm |
3.00 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 151 °C | 304 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 146 °C | 295 °F | ASTM D648 |
Users viewing this material also viewed the following:
- Premix Premi-Glas® 3200-20 Fiberglass Reinforced SMC
- PolyMirae Moplen EP332C Pipe Extrusion Grade Polypropylene
- Kinlead PG14 Bag Grade BOPP Plain Film (thickness: 30 µm)
- Lanxess Durethan® BKV 15 H2.0 901510 Copolyamide, 15% Glass Fiber
- Lehmann & Voss LUVOCOM® 1105-8389/BL PEEK, with glass fiber
- Spartech E65050 General Purpose PVC
- A. Schulman POLYBATCH™ CE-505-E Concentrate Based In Polyethylene
- Entec Hylex® P1302B Polycarbonate
- Asahi Kasei Thermylon® NSG-240A 50% Ceramic and Glass Fiber Reinforced
- Karina E 57/200-D-AT-IS-SI-SD Clear PVC Compound
Copyright © lookpolymers.com All Rights Reserved