LATI Latene® AG3H2W G/30-V0E PP Homopolymer, 30% Glass Fiber Reinforced, Heat Stabilized, Flame Retardant

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 30% Glass Fiber Filler , Polypropylene, Flame Retardant
Manufacturer LATI
Trade Name Latene®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Latene® AG3H2W G/30-V0E PP Homopolymer, 30% Glass Fiber Reinforced, Heat Stabilized, Flame Retardant.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polypropylene homopolymer (PPh) based compound. Chemical grafting Heat stabilized. Metal stabilized. Glass fibers. UL94 V-0 classified, with brominated flame retardants, PBB/PBDE freeAvailability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.46 g/cc
0.0527 lb/in³
Linear Mold Shrinkage, Flow 0.0030 - 0.0050 cm/cm
0.0030 - 0.0050 in/in
Linear Mold Shrinkage, Transverse 0.0075 - 0.0095 cm/cm
0.0075 - 0.0095 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 30.0 MPa

@Temperature 90.0 °C
 4350 psi

@Temperature 194 °F
45.0 MPa

@Temperature 60.0 °C
 6530 psi

@Temperature 140 °F
75.0 MPa

@Temperature 23.0 °C
 10900 psi

@Temperature 73.4 °F
Elongation at Break 2.5 %

@Temperature 23.0 °C
 2.5 %

@Temperature 73.4 °F
4.0 %

@Temperature 60.0 °C
 4.0 %

@Temperature 140 °F
7.0 %

@Temperature 90.0 °C
 7.0 %

@Temperature 194 °F
Elongation at Yield 2.5 %

@Temperature 60.0 °C
 2.5 %

@Temperature 140 °F
4.0 %

@Temperature 90.0 °C
 4.0 %

@Temperature 194 °F
Tensile Modulus 4.30 GPa

@Temperature 90.0 °C
 624 ksi

@Temperature 194 °F
5.70 GPa

@Temperature 60.0 °C
 827 ksi

@Temperature 140 °F
7.80 GPa

@Temperature 23.0 °C
 1130 ksi

@Temperature 73.4 °F
Charpy Impact Unnotched 2.00 J/cm²

@Temperature -20.0 °C
 9.52 ft-lb/in²

@Temperature -4.00 °F
4.00 J/cm²

@Temperature 23.0 °C
 19.0 ft-lb/in²

@Temperature 73.4 °F
Charpy Impact, Notched 0.500 J/cm²

@Temperature -20.0 °C
 2.38 ft-lb/in²

@Temperature -4.00 °F
1.00 J/cm²

@Temperature 23.0 °C
 4.76 ft-lb/in²

@Temperature 73.4 °F
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 110 °C
230 °F
Deflection Temperature at 0.46 MPa (66 psi) 155 °C
311 °F
Deflection Temperature at 1.8 MPa (264 psi) 140 °C
284 °F
Vicat Softening Point 135 °C

@Load 5.00 kg
 275 °F

@Load 11.0 lb
Flammability, UL94 V-0

@Thickness 3.00 mm
 V-0

@Thickness 0.118 in
V-0

@Thickness 1.50 mm
 V-0

@Thickness 0.0591 in
V-0

@Thickness 0.750 mm
 V-0

@Thickness 0.0295 in
Oxygen Index 26 %
26 %
Electrical Properties Metric English Comments
Comparative Tracking Index 575 V
575 V
A solution
Processing Properties Metric English Comments
Melt Temperature 190 - 220 °C
374 - 428 °F
Mold Temperature 30.0 - 50.0 °C
86.0 - 122 °F
Drying Temperature 80.0 - 90.0 °C

@Time 10800 sec
 176 - 194 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa