LATI Latamid SP1 PA 6.10
| Category | Polymer , Thermoplastic , Nylon , Nylon 610 |
| Manufacturer | LATI |
| Trade Name | Latamid |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LATI Latamid SP1 PA 6.10.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Polyamide 6.10 (PA6.10). Unfilled. Low moisture absorption.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.07 g/cc | 0.0387 lb/in³ | |
| Linear Mold Shrinkage, Flow | 0.010 - 0.014 cm/cm | 0.010 - 0.014 in/in | |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.014 cm/cm | 0.010 - 0.014 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 60.0 MPa | 8700 psi | |
| Elongation at Break | >= 100 % @Temperature 60.0 °C |
>= 100 % @Temperature 140 °F |
|
| >= 100 % @Temperature 90.0 °C |
>= 100 % @Temperature 194 °F |
||
| >= 100 % @Temperature 120 °C |
>= 100 % @Temperature 248 °F |
||
| >= 100 % @Temperature 150 °C |
>= 100 % @Temperature 302 °F |
||
| 100 % @Temperature 23.0 °C |
100 % @Temperature 73.4 °F |
||
| Tensile Modulus | 0.200 GPa @Temperature 150 °C |
29.0 ksi @Temperature 302 °F |
|
| 0.300 GPa @Temperature 120 °C |
43.5 ksi @Temperature 248 °F |
||
| 0.450 GPa @Temperature 90.0 °C |
65.3 ksi @Temperature 194 °F |
||
| 0.700 GPa @Temperature 60.0 °C |
102 ksi @Temperature 140 °F |
||
| 2.40 GPa @Temperature 23.0 °C |
348 ksi @Temperature 73.4 °F |
||
| Charpy Impact Unnotched | NB | NB | |
| Charpy Impact, Notched | 0.600 J/cm² | 2.86 ft-lb/in² |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 70.0 °C | 158 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 175 °C | 347 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 65.0 °C | 149 °F | |
| Vicat Softening Point | 180 °C @Load 5.00 kg |
356 °F @Load 11.0 lb |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 230 - 260 °C | 446 - 500 °F | |
| Mold Temperature | 70.0 - 90.0 °C | 158 - 194 °F | |
| Drying Temperature | 70.0 - 90.0 °C @Time 7200 sec |
158 - 194 °F @Time 2.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| ISO Shrinkage - Pressure | 60 MPa |
Users viewing this material also viewed the following:
- MV Labs FE165 K4Fe(CN)6·xH2O Potassium ferrocyanide(II) hydrate
- IRPC Polimaxx Porene GA800 Acrylonitrile Butadiene Styrene
- SGL Carbon Group PANOX® FM C063 EEA Oxidized Textile Fiber, Crimped staple fiber, For carbon/carbon and spinning
- Sawbones Laminated Test Blocks
- Wellman Wellamid® 42LH-N Unfilled Nylon 6, Lubricated & Heat Stabilized
- Hexcel® HexForce™ GA090 Carbon Fabric
- Polyram RamSter PF321G6 PBT, 30% Glass Fiber, Flame Retardant
- Braskem H 214 HOMO Polypropylene Homopolymer
Copyright © lookpolymers.com All Rights Reserved