LATI Latamid 66 S/30 PA 66, 30% Glass Bead Reinforced

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Glass Bead Filled
Manufacturer LATI
Trade Name Latamid
Port Shanghai port,China
Trade Terms EXW, FOB, CFR, CIF
Payment Terms L/C, T/T, PayPal
Download PDF LATI Latamid 66 S/30 PA 66, 30% Glass Bead Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
Polyamide 66 (PA66) based compound. Glass beads. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.39 g/cc
0.0502 lb/in³
Linear Mold Shrinkage, Flow 0.0090 - 0.012 cm/cm
0.0090 - 0.012 in/in
Linear Mold Shrinkage, Transverse 0.0090 - 0.012 cm/cm
0.0090 - 0.012 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 25.0 MPa
<br>@Temperature 150 °C
 3630 psi
<br>@Temperature 302 °F
30.0 MPa
<br>@Temperature 120 °C
 4350 psi
<br>@Temperature 248 °F
40.0 MPa
<br>@Temperature 90.0 °C
 5800 psi
<br>@Temperature 194 °F
55.0 MPa
<br>@Temperature 60.0 °C
 7980 psi
<br>@Temperature 140 °F
85.0 MPa
<br>@Temperature 23.0 °C
 12300 psi
<br>@Temperature 73.4 °F
Elongation at Break 5.0 %
<br>@Temperature 23.0 °C
 5.0 %
<br>@Temperature 73.4 °F
15 %
<br>@Temperature 60.0 °C
 15 %
<br>@Temperature 140 °F
20 %
<br>@Temperature 90.0 °C
 20 %
<br>@Temperature 194 °F
25 %
<br>@Temperature 120 °C
 25 %
<br>@Temperature 248 °F
45 %
<br>@Temperature 150 °C
 45 %
<br>@Temperature 302 °F
Elongation at Yield 10 %
<br>@Temperature 60.0 °C
 10 %
<br>@Temperature 140 °F
14 %
<br>@Temperature 90.0 °C
 14 %
<br>@Temperature 194 °F
15 %
<br>@Temperature 120 °C
 15 %
<br>@Temperature 248 °F
16 %
<br>@Temperature 150 °C
 16 %
<br>@Temperature 302 °F
Tensile Modulus 0.640 GPa
<br>@Temperature 150 °C
 92.8 ksi
<br>@Temperature 302 °F
0.800 GPa
<br>@Temperature 120 °C
 116 ksi
<br>@Temperature 248 °F
1.20 GPa
<br>@Temperature 90.0 °C
 174 ksi
<br>@Temperature 194 °F
2.20 GPa
<br>@Temperature 60.0 °C
 319 ksi
<br>@Temperature 140 °F
4.70 GPa
<br>@Temperature 23.0 °C
 682 ksi
<br>@Temperature 73.4 °F
Charpy Impact Unnotched 1.50 J/cm²
<br>@Temperature -20.0 °C
 7.14 ft-lb/in²
<br>@Temperature -4.00 °F
2.00 J/cm²
<br>@Temperature 23.0 °C
 9.52 ft-lb/in²
<br>@Temperature 73.4 °F
Charpy Impact, Notched 0.0800 J/cm²
<br>@Temperature -20.0 °C
 0.381 ft-lb/in²
<br>@Temperature -4.00 °F
0.200 J/cm²
<br>@Temperature 23.0 °C
 0.952 ft-lb/in²
<br>@Temperature 73.4 °F
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 90.0 °C
194 °F
Deflection Temperature at 0.46 MPa (66 psi) 230 °C
446 °F
Deflection Temperature at 1.8 MPa (264 psi) 140 °C
284 °F
Vicat Softening Point 225 °C
<br>@Load 5.00 kg
 437 °F
<br>@Load 11.0 lb
Processing Properties Metric English Comments
Melt Temperature 275 - 300 °C
527 - 572 °F
Mold Temperature 80.0 - 100 °C
176 - 212 °F
Drying Temperature 90.0 - 100 °C
<br>@Time 10800 sec
 194 - 212 °F
<br>@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa
Users viewing this material also viewed the following: