- Kolon KOPA® KN132G15VO G/F Reinforced Flame Retardant Nylon 6
Kolon KOPA® KN132G15VO G/F Reinforced Flame Retardant Nylon 6
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Glass Fiber Filled, Flame Retardant |
| Manufacturer | Kolon |
| Trade Name | Kopa® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Kolon KOPA® KN132G15VO G/F Reinforced Flame Retardant Nylon 6.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
KOPA® is a thermoplastic resin with excellent mechanical, thermal and electrical properties and is widely used in automobile and industrial parts.Good mechanical properties, outstanding self-lubrication and abrasion resistance, excellent chemical resistance, wide usage temperature, good impact absorbing characteristicsInformation provided by US distributor, API-Kolon.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.30 g/cc | 0.0470 lb/in³ | DIN 53479; ASTM D792 |
| Water Absorption | 0.70 % | 0.70 % | DIN 53475; ASTM D570 |
| Linear Mold Shrinkage | 0.0070 - 0.0080 cm/cm | 0.0070 - 0.0080 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | DIN 53505; ASTM D785 |
| Tensile Strength, Ultimate | 118 MPa | 17100 psi | DIN 53455; ASTM D638 |
| Elongation at Break | 5.0 % | 5.0 % | DIN 53455; ASTM D638 |
| Flexural Yield Strength | 157 MPa | 22800 psi | DIN 53455; ASTM D790 |
| Flexural Modulus | 5.88 GPa | 853 ksi | DIN 53452; ASTM D790 |
| Izod Impact, Notched | 0.588 J/cm | 1.10 ft-lb/in | DIN 53453; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 80.0 µm/m-°C @Temperature 20.0 °C |
44.4 µin/in-°F @Temperature 68.0 °F |
DIN 53752; ASTM D696 |
| Melting Point | 220 °C | 428 °F | DIN 53736; ASTM D789 |
| Deflection Temperature at 0.46 MPa (66 psi) | 205 °C | 401 °F | DIN 53461; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 195 °C | 383 °F | DIN 53461; ASTM D648 |
| Flammability, UL94 | V-0 | V-0 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 3.8 @Frequency 1e+6 Hz |
3.8 @Frequency 1e+6 Hz |
ASTM D150/DIN 53483 |
| Dielectric Strength | 21.0 kV/mm | 533 kV/in | ASTM D149/DIN 53481 |
| Arc Resistance | 130 sec | 130 sec | ASTM D495 |
Users viewing this material also viewed the following:
- RheTech Products F15-01 35% Glass Fiber Reinforced Polypropylene, Chemically Coupled, Black
- Huntsman PE7076 Profile Extrusion Polyethylene (discontinued **)
- Karina E 18/548-RG-GE Gray Color Concentrate for PVC
- PCP-Canada ALCA MAX® 2XXX Cast Aluminum Mold Blocks/Plate
- Wellman Wellamid® GFT1702-WBK1 33% Glass Fiber Reinforced, Impact Modified and Weatherable Nylon 66
- Formosa Plastics Formolene® 5144H Homopolymer Polypropylene
- ELASTO UK Dryflex® 502550S SEBS Based Material, Unfilled Qualities, 55A Hardness, Black
- DuPont Performance Polymers Zytel® HTN 54G35EF NC010 Polyphthalamide (PPA)
Copyright © lookpolymers.com All Rights Reserved