Kolon KOCETAL® TC702 Mineral Reinforced Acetal Resin
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Mineral Filled |
| Manufacturer | Kolon |
| Trade Name | Kocetal® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Kolon KOCETAL® TC702 Mineral Reinforced Acetal Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Talc reinforced, improved dimensional stability. Applications: Products for high stiffness, dimensional precision. Information provided by API-Kolon.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.48 g/cc | 1.48 g/cc | ASTM D792 |
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | 60% RH; ASTM D570 |
| Linear Mold Shrinkage | 0.017 cm/cm | 0.017 in/in | ASTM D955 |
| Melt Flow | 22 g/10 min | 22 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 82 | 82 | ASTM D785 |
| Tensile Strength | 62.0 MPa | 8990 psi | ASTM D638 |
| Elongation at Break | 14 % | 14 % | ASTM D638 |
| Flexural Strength | 105 MPa | 15200 psi | ASTM D790 |
| Flexural Modulus | 3.60 GPa | 522 ksi | ASTM D790 |
| Izod Impact, Notched | 0.400 J/cm | 0.749 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 80.0 µm/m-°C | 44.4 µin/in-°F | ASTM D696 |
| Melting Point | 166 °C | 331 °F | ASTM D1525 |
| Deflection Temperature at 0.46 MPa (66 psi) | 162 °C | 324 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 135 °C | 275 °F | ASTM D648 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | ASTM D257 |
| Surface Resistance | 1.00e+16 ohm | 1.00e+16 ohm | ASTM D257 |
| Dielectric Constant | 3.7 | 3.7 | ASTM D150 |
| Dielectric Strength | 19.0 kV/mm | 483 kV/in | ASTM D149 |
| Dissipation Factor | 0.0060 @Frequency 1.00e+6 Hz |
0.0060 @Frequency 1.00e+6 Hz |
ASTM D150 |
Users viewing this material also viewed the following:
- Multibase Multi-Pro® 2012 RC 20% Glass Filled Polypropylene
- Plastcom SLOVAMID 66 GF 30 FRA 5 Polyamide 66, 30% Glass Fiber, Halogen Flame Retardant
- Lord Adhesives 7545D Two-Component, Equal-Mix, Non-Sag Urethane Adhesive
- Momentive Performance Materials RTV6445 Heat-Curing Silicone Adhesive, White
- Zotefoams Plastazote® LD30SD Static Dissipative Low Density Polyethylene Foam
- Eastman Eastar GN119 Copolyester
- ELASTO UK Dryflex® 500800S SEBS Based Material, Unfilled Qualities, 80A Hardness, Translucent
- DuPont™ Entira® AS500 Ionomer Resin
- SABIC Innovative Plastics Lexan® EXRL0681 PC Copolymer
Copyright © lookpolymers.com All Rights Reserved