- Kolon KOCETAL® GB705 Glass Bead Reinforced Acetal Resin
Kolon KOCETAL® GB705 Glass Bead Reinforced Acetal Resin
| Category | Polymer , Thermoplastic , Acetal (POM) |
| Manufacturer | Kolon |
| Trade Name | Kocetal® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Kolon KOCETAL® GB705 Glass Bead Reinforced Acetal Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Glass bead added, improved dimensional stability. Applications: Products for high stiffness, dimensional precision. Information provided by API-Kolon.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.59 g/cc | 1.59 g/cc | ASTM D792 |
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | 60% RH; ASTM D570 |
| Linear Mold Shrinkage | 0.017 cm/cm | 0.017 in/in | ASTM D955 |
| Melt Flow | 23 g/10 min | 23 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 82 | 82 | ASTM D785 |
| Tensile Strength | 43.0 MPa | 6240 psi | ASTM D638 |
| Elongation at Break | 25 % | 25 % | ASTM D638 |
| Flexural Strength | 85.0 MPa | 12300 psi | ASTM D790 |
| Flexural Modulus | 3.50 GPa | 508 ksi | ASTM D790 |
| Izod Impact, Notched | 0.300 J/cm | 0.562 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 80.0 µm/m-°C | 44.4 µin/in-°F | ASTM D696 |
| Melting Point | 166 °C | 331 °F | ASTM D1525 |
| Deflection Temperature at 0.46 MPa (66 psi) | 163 °C | 325 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 120 °C | 248 °F | ASTM D648 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | ASTM D257 |
| Surface Resistance | 1.00e+16 ohm | 1.00e+16 ohm | ASTM D257 |
| Dielectric Constant | 3.7 | 3.7 | ASTM D150 |
| Dielectric Strength | 19.0 kV/mm | 483 kV/in | ASTM D149 |
| Dissipation Factor | 0.0060 @Frequency 1.00e+6 Hz |
0.0060 @Frequency 1.00e+6 Hz |
ASTM D150 |
Users viewing this material also viewed the following:
- RheTech Products HP519-00 26% Talc Reinforced High Performance Polypropylene Copolymer, Non-UV Stabilized, Natural
- Pyrotek R-3C Silicone Coated Rope
- Polymer Resources PEI-GP1 Polyetherimide, Flame Retardant
- Polymer Resources NY66-IMG33-[color]H Nylon, 33% Glass Reinforced, Impact Modified, Heat Stabilized (DAM)
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 1.0 PHR MBTS
- 3M Dyneon™ TF 5050 PTFE Dispersion (discontinued **)
- Inno-Comp INNOPOL® CS 2-9523 20% Talc-Filled, Elastomer Modified Polypropylene Block-Copolymer
- Seals Eastern 5483 Nitrile Rubber
- Saint-Gobain COHRlastic® CF4032 General Purpose Reinforced Solid Rubber
- A. Schulman POLYBATCH™ Yellow 2946ST Concentrate Based In Polyethylene
Copyright © lookpolymers.com All Rights Reserved