Polykemi AB POLYshine PBT D233 GF15 FR Polypropylene, Glass Fiber Reinforced, Flame Retardant

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 20% Glass Fiber Filler
Manufacturer Polykemi AB
Trade Name POLYshine
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polykemi AB POLYshine PBT D233 GF15 FR Polypropylene, Glass Fiber Reinforced, Flame Retardant.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by Polykemi AB
Physical Properties Metric English Comments
Density 1.43 g/cc
0.0517 lb/in³
ISO 1183
Filler Content 15 %
15 %
±2%; Polykemi
Linear Mold Shrinkage 0.0040 cm/cm
0.0040 in/in
With Flow; ISO 2577
0.013 cm/cm
0.013 in/in
Across Flow; ISO 2577
Mechanical Properties Metric English Comments
Tensile Strength at Break <= 115 MPa
<= 16700 psi
ISO/R527
Elongation at Break 2.5 %
2.5 %
ISO/R527
Flexural Strength <= 165 MPa
<= 23900 psi
ISO 178
Flexural Modulus 6.00 GPa

@Temperature 23.0 °C
 870 ksi

@Temperature 73.4 °F
 ISO 178
Charpy Impact, Notched 0.500 J/cm²

@Temperature 23.0 °C
 2.38 ft-lb/in²

@Temperature 73.4 °F
 ISO 179
0.500 J/cm²

@Temperature -20.0 °C
 2.38 ft-lb/in²

@Temperature -4.00 °F
 ISO 179
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 205 °C
401 °F
120°C/h; ISO 75/1
Deflection Temperature at 1.8 MPa (264 psi) 190 °C
374 °F
120°C/h; ISO 75/1
Vicat Softening Point 205 °C

@Load 5.001 kg
 401 °F

@Load 11.03 lb
 50°C/h; ISO 306
Flammability, UL94 V-0

@Thickness 1.60 mm
 V-0

@Thickness 0.0630 in
Glow Wire Test 960 °C

@Thickness 2.00 mm
 1760 °F

@Thickness 0.0787 in
 IEC 695-2-1