Kingfa NH-627 Flame Retardant ABS

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Unreinforced, Flame Retardant
Manufacturer Kingfa Sci. & Tech. Co.
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Kingfa NH-627 Flame Retardant ABS.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Features:UL 94 V-2 @ 1.6mmHalogen-free flame retardantHigh flowApplications:OA deviceDigital cameraVidiconInformation Provided by Kingfa Sci. & Tech. Co., Ltd.
Physical Properties Metric English Comments
Specific Gravity 1.06 g/cc

@Temperature 23.0 °C
 1.06 g/cc

@Temperature 73.4 °F
 ASTM D792
Linear Mold Shrinkage 0.0040 - 0.0070 cm/cm

@Temperature 23.0 °C
 0.0040 - 0.0070 in/in

@Temperature 73.4 °F
 ASTM D955
Melt Flow 5.0 g/10 min

@Load 5.00 kg,
Temperature 200 °C
 5.0 g/10 min

@Load 11.0 lb,
Temperature 392 °F
 ASTM D1238
55 g/10 min

@Load 10.0 kg,
Temperature 220 °C
 55 g/10 min

@Load 22.0 lb,
Temperature 428 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 102
102
ASTM D785
Tensile Strength at Break 45.0 MPa
6530 psi
50mm/min; ASTM D638
Elongation at Break 10 %
10 %
50mm/min; ASTM D638
Flexural Strength 70.0 MPa
10200 psi
2mm/min; ASTM D790
Flexural Modulus 2.50 GPa
363 ksi
2mm/min; ASTM D790
Izod Impact, Notched 1.25 J/cm

@Thickness 6.40 mm,
Temperature 23.0 °C
 2.34 ft-lb/in

@Thickness 0.252 in,
Temperature 73.4 °F
 ASTM D256
1.45 J/cm

@Thickness 3.20 mm,
Temperature 23.0 °C
 2.72 ft-lb/in

@Thickness 0.126 in,
Temperature 73.4 °F
 ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 80.0 °C

@Thickness 6.40 mm
 176 °F

@Thickness 0.252 in
 ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 72.0 °C

@Thickness 6.40 mm
 162 °F

@Thickness 0.252 in
 ASTM D648
Vicat Softening Point 81.0 °C

@Load 5.00 kg
 178 °F

@Load 11.0 lb
 50°C/min; ASTM D1525
90.0 °C

@Load 1.00 kg
 194 °F

@Load 2.20 lb
 120°C/min; ASTM D1525
Flammability, UL94 V-2

@Thickness 1.60 mm
 V-2

@Thickness 0.0630 in
V-2

@Thickness 0.800 mm
 V-2

@Thickness 0.0315 in
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+14 ohm-cm
1.00e+14 ohm-cm
ASTM D257
Dielectric Strength 22.0 kV/mm
559 kV/in
ASTM D149
Processing Properties Metric English Comments
Processing Temperature <= 250 °C
<= 482 °F
Rear Barrel Temperature 180 - 200 °C
356 - 392 °F
Start Point: 190°C
Middle Barrel Temperature 190 - 210 °C
374 - 410 °F
Start Point: 200°C
Front Barrel Temperature 195 - 220 °C
383 - 428 °F
Start Point: 210°C
Melt Temperature 200 - 230 °C
392 - 446 °F
Start Point: 215°C
Mold Temperature 30.0 - 60.0 °C
86.0 - 140 °F
Start Point: 50°C
Drying Temperature 70.0 °C

@Time 7200 sec
 158 °F

@Time 2.00 hour
 Pre-dry
Back Pressure 0.000 - 1.00 MPa
0.000 - 145 psi
Descriptive Properties Value Comments
Injection Speed Slow to Moderate