- Kingfa JH710 G15 Flame Retardant & 15% Glass Fiber Reinforced PC
Kingfa JH710 G15 Flame Retardant & 15% Glass Fiber Reinforced PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Glass Fiber Filled, Flame Retardant |
| Manufacturer | Kingfa Sci. & Tech. Co. |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Kingfa JH710 G15 Flame Retardant & 15% Glass Fiber Reinforced PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Features:Environmental friendly flame retardantUL V-0 @ 1.6mmHigh mechanical strengthGood size stability, good surfaceSuitable for exact moldingApplications:CD-ROM, DVDPrinter, photocopier cabinetScanner partsExact mechanism partsElectrical equipment partsInformation Provided by Kingfa Sci. & Tech. Co., Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.31 g/cc @Temperature 23.0 °C |
1.31 g/cc @Temperature 73.4 °F |
ASTM D792 |
| Linear Mold Shrinkage | 0.0030 - 0.0040 cm/cm @Temperature 23.0 °C |
0.0030 - 0.0040 in/in @Temperature 73.4 °F |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 84 | 84 | ASTM D785 |
| Tensile Strength at Break | 90.0 MPa | 13100 psi | 10mm/min; ASTM D638 |
| Elongation at Break | 7.0 % | 7.0 % | 10mm/min; ASTM D638 |
| Flexural Strength | 138 MPa | 20000 psi | 2mm/min; ASTM D790 |
| Flexural Modulus | 5.50 GPa | 798 ksi | 2mm/min; ASTM D790 |
| Izod Impact, Notched | 0.920 J/cm @Thickness 3.20 mm, Temperature -30.0 °C |
1.72 ft-lb/in @Thickness 0.126 in, Temperature -22.0 °F |
ASTM D256 |
| 1.09 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
2.04 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 144 °C @Thickness 6.40 mm |
291 °F @Thickness 0.252 in |
ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 132 °C @Thickness 6.40 mm |
270 °F @Thickness 0.252 in |
ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 1.60 mm |
V-0 @Thickness 0.0630 in |
|
| V-0 @Thickness 3.00 mm |
V-0 @Thickness 0.118 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Surface Resistance | 1.00e+16 ohm | 1.00e+16 ohm | ASTM D257 |
| Dielectric Strength | 19.0 kV/mm | 483 kV/in | 1.6mm; ASTM D149 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | <= 290 °C | <= 554 °F | |
| Rear Barrel Temperature | 230 - 250 °C | 446 - 482 °F | Start Point: 240°C |
| Middle Barrel Temperature | 235 - 260 °C | 455 - 500 °F | Start Point: 245°C |
| Front Barrel Temperature | 240 - 270 °C | 464 - 518 °F | Start Point: 250°C |
| Melt Temperature | 235 - 260 °C | 455 - 500 °F | Start Point: 240°C |
| Mold Temperature | 80.0 - 130 °C | 176 - 266 °F | Start Point: 90°C |
| Drying Temperature | 110 - 120 °C @Time 10800 - 14400 sec |
230 - 248 °F @Time 3.00 - 4.00 hour |
Pre-dry |
| Back Pressure | 0.300 - 1.00 MPa | 43.5 - 145 psi |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Glass Fiber Content (%) | 15 | |
| Injection Speed | 60-90% |
Users viewing this material also viewed the following:
- Loxim 200 00HB Polybutylene Terephthalate
- Lubrizol Advanced Materials Pearlthane® D91F88 Thermoplastic Polyurethane Elastomer
- JPJ Technologies 8200B HDPE Blow Molding
- LG Chemical LUPOL TE-5104K Thermoplastic Elastomer Alloy, 10% Polymer Alloy, High Modulus
- Gromax BTE70-DN001N1 Nylon 6 (Dry)
- Techmer ES Elastoblend® PA6 GF34 IM HS 34% Glass Filled
- California Fine Wire Alloy 443 Precious Metal Alloy
- 3M FP032302W White Metallized Polypropylene Label Products
Copyright © lookpolymers.com All Rights Reserved