Kennametal Stellite Stellite® 3 PM with P/M Processing

Category Metal , Nonferrous Metal , Cobalt Alloy , Superalloy
Manufacturer Kennametal Stellite
Trade Name Stellite®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Kennametal Stellite Stellite® 3 PM with P/M Processing.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Typical applications include (aerospace) vane plugs, fuel metering pins, spacer bushings, (bearings) ball blanks, race blanks, (valve seat inserts) diesel engine exhaust, fluid valve seats, saw cutter inserts, miscellaneous wear parts. Adhesive wear test data: P/M 0.10, Cast 0.24. Data provided by the manufacturer, Deloro Stellite Inc.Product of former Deloro Stellite Inc.
Physical Properties Metric English Comments
Density 8.40 g/cc
0.303 lb/in³
P/M (97%); 8.64 g/cc theoretical
Mechanical Properties Metric English Comments
Hardness, Brinell 533
533
Converted from Rockwell C hardness.
271

@Temperature 760 °C
 271

@Temperature 1400 °F
 Converted from Rockwell C hardness
354

@Temperature 649 °C
 354

@Temperature 1200 °F
 Converted from Rockwell C hardness
427

@Temperature 538 °C
 427

@Temperature 1000 °F
 Converted from Rockwell C hardness
Hardness, Knoop 643
643
Converted from Rockwell C hardness.
321

@Temperature 760 °C
 321

@Temperature 1400 °F
 Converted from Rockwell C hardness
424

@Temperature 649 °C
 424

@Temperature 1200 °F
 Converted from Rockwell C hardness
513

@Temperature 538 °C
 513

@Temperature 1000 °F
 Converted from Rockwell C hardness
Hardness, Rockwell A 77
77
Converted from Rockwell C hardness.
64

@Temperature 760 °C
 64

@Temperature 1400 °F
 Converted from Rockwell C hardness
70

@Temperature 649 °C
 70

@Temperature 1200 °F
 Converted from Rockwell C hardness
73

@Temperature 538 °C
 73

@Temperature 1000 °F
 Converted from Rockwell C hardness
Hardness, Rockwell C 54
54
Hot hardness.
28

@Temperature 760 °C
 28

@Temperature 1400 °F
 Hot hardness.
39

@Temperature 649 °C
 39

@Temperature 1200 °F
 Hot hardness.
46

@Temperature 538 °C
 46

@Temperature 1000 °F
 Hot hardness.
Hardness, Vickers 575
575
Converted from Rockwell C hardness.
280

@Temperature 760 °C
 280

@Temperature 1400 °F
 Converted from Rockwell C hardness
372

@Temperature 649 °C
 372

@Temperature 1200 °F
 Converted from Rockwell C hardness
454

@Temperature 538 °C
 454

@Temperature 1000 °F
 Converted from Rockwell C hardness
Tensile Strength, Ultimate 863 MPa
125000 psi
621 MPa

@Temperature 760 °C
 90100 psi

@Temperature 1400 °F
690 MPa

@Temperature 649 °C
 100000 psi

@Temperature 1200 °F
725 MPa

@Temperature 538 °C
 105000 psi

@Temperature 1000 °F
Elongation at Break <= 1.0 %
<= 1.0 %
in 25.4 mm
Thermal Properties Metric English Comments
CTE, linear 12.3 µm/m-°C

@Temperature 0.000 - 100 °C
 6.83 µin/in-°F

@Temperature 32.0 - 212 °F
12.5 µm/m-°C

@Temperature 0.000 - 200 °C
 6.94 µin/in-°F

@Temperature 32.0 - 392 °F
12.7 µm/m-°C

@Temperature 0.000 - 300 °C
 7.06 µin/in-°F

@Temperature 32.0 - 572 °F
12.9 µm/m-°C

@Temperature 0.000 - 400 °C
 7.17 µin/in-°F

@Temperature 32.0 - 752 °F
13.0 µm/m-°C

@Temperature 0.000 - 500 °C
 7.22 µin/in-°F

@Temperature 32.0 - 932 °F
13.1 µm/m-°C

@Temperature 0.000 - 600 °C
 7.28 µin/in-°F

@Temperature 32.0 - 1110 °F
13.4 µm/m-°C

@Temperature 0.000 - 700 °C
 7.44 µin/in-°F

@Temperature 32.0 - 1290 °F
13.7 µm/m-°C

@Temperature 0.000 - 800 °C
 7.61 µin/in-°F

@Temperature 32.0 - 1470 °F
14.5 µm/m-°C

@Temperature 0.000 - 900 °C
 8.06 µin/in-°F

@Temperature 32.0 - 1650 °F
16.0 µm/m-°C

@Temperature 0.000 - 1000 °C
 8.89 µin/in-°F

@Temperature 32.0 - 1830 °F
Melting Point 1213 - 1285 °C
2215 - 2345 °F
Solidus 1213 °C
2215 °F
Liquidus 1285 °C
2345 °F
Component Elements Properties Metric English Comments
Boron, B <= 1.0 %
<= 1.0 %
Carbon, C 2.4 %
2.4 %
Chromium, Cr 31 %
31 %
Cobalt, Co 44 %
44 %
As remainder
Iron, Fe <= 3.0 %
<= 3.0 %
Manganese, Mn <= 1.0 %
<= 1.0 %
Nickel, Ni <= 3.0 %
<= 3.0 %
Other <= 1.0 %
<= 1.0 %
Silicon, Si <= 1.0 %
<= 1.0 %
Tungsten, W 12.5 %
12.5 %
Electrical Properties Metric English Comments
Magnetic Permeability <= 1.20

@Temperature 22.0 °C
 <= 1.20

@Temperature 71.6 °F
 200 Oersted