Lanxess Pocan® KU 2-7209 Z 000000 PBT, 15% Glass Fiber
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 20% Glass Fiber Filled |
| Manufacturer | Lanxess |
| Trade Name | Pocan® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Pocan® KU 2-7209 Z 000000 PBT, 15% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PBT, 15% glass fibers, injection molding, flame retardant, impact modified
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.55 g/cc | 0.0560 lb/in³ | ISO 1183 |
| Water Absorption | 0.40 % | 0.40 % | Test Sim. to ISO 62 |
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | 23°C/50% R.H.; Test Sim. to ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0090 cm/cm | 0.0090 in/in | ISO 294-4, 2577 |
| Linear Mold Shrinkage, Transverse | 0.0011 cm/cm | 0.0011 in/in | ISO 294-4, 2577 |
| Melt Flow | 31 g/10 min @Load 5.00 kg, Temperature 260 °C |
31 g/10 min @Load 11.0 lb, Temperature 500 °F |
Estimated using room temperature density; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 92.0 MPa | 13300 psi | ISO 527-1/-2 |
| Tensile Strength, Yield | 95.0 MPa | 13800 psi | ISO 527-1/-2 |
| Elongation at Break | 3.0 % | 3.0 % | ISO 527-1/-2 |
| Elongation at Yield | 3.0 % | 3.0 % | ISO 527-1/-2 |
| Tensile Modulus | 6.20 GPa | 899 ksi | ISO 527-1/-2 |
| Charpy Impact Unnotched | 5.00 J/cm² @Temperature 23.0 °C |
23.8 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU |
| Charpy Impact, Notched | <= 1.00 J/cm² @Temperature 23.0 °C |
<= 4.76 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 40.0 µm/m-°C | 22.2 µin/in-°F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 110 µm/m-°C | 61.1 µin/in-°F | ISO 11359-1/-2 |
| Melting Point | 225 °C | 437 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 172 °C | 342 °F | ISO 75-1/-2 |
| Deflection Temperature at 8.0 MPa | 70.0 °C | 158 °F | ISO 75-1/-2 |
| Vicat Softening Point | 205 °C | 401 °F | 50°C/h 50N; ISO 306 |
| Flammability, UL94 | V-0 @Thickness 0.750 mm |
V-0 @Thickness 0.0295 in |
IEC 60695-11-10 |
| V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
IEC 60695-11-10 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | 250 V | 250 V | IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 260 °C | 500 °F | Injection Molding; ISO 294 |
| Mold Temperature | 80.0 °C | 176 °F | Injection Molding; ISO 10724 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Additives | Flame retarding agent | |
| Features | Flame retardant | |
| High impact or high impact modified | ||
| Form | Pellets | |
| ISO Shortname | ISO 7792-1-PBT,GFHMPR,09-060,GF15; ISO 1043-PBT GF FR(17) | |
| Processing | Injection molding | |
| Region | Asia Pacific | |
| Europe | ||
| Near East/Africa | ||
| North America | ||
| South and Central America |
Users viewing this material also viewed the following:
- Technetics Group Amicon™ PET-P (Unverified Data**)
- LyondellBasell Alathon® H4250 High Density Polyethylene, Injection Molding Grade
- Lucite International Elvacite ® 2927 Acrylic Resin
- Sylvin Technologies 9600-60 Clear PVC Molding Compound
- SABIC Innovative Plastics LNP STAT-LOY AF3009 ABS (Asia Pacific)
- SABIC Innovative Plastics LNP Thermocomp PH0600B PA 6 (Asia Pacific)
- Tipco Tipcolite® TG 311 Phenolic Compound, Mineral & Wood Flour, Medium Flow & High Electrical Properties
- Diapolyacrylate Acrypet® VH-001 Heat Stabilized PMMA
- Beijing Chemical Industry KAIFA® M109-G20N MPPO Resin
- BASF Ultramid® A3HG6 Balance 30% Glass Filled PA 66/610 (Conditioned)
Copyright © lookpolymers.com All Rights Reserved