Kazanorgsintez 271-274K Cable Composition Based on High Density Polyethylene
| Category | Polymer , Thermoplastic , Polyethylene (PE) , HDPE |
| Manufacturer | Kazanorgsintez |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Kazanorgsintez 271-274K Cable Composition Based on High Density Polyethylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Production Method: Gaseous-phase method. Application: Compositions are intended for cover insulating lapping, protective covers and cables.Information Provided by Kazanorgsintez
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.950 - 0.955 g/cc | 0.0343 - 0.0345 lb/in³ | |
| Volatiles | <= 0.000010 % | <= 0.000010 % | Superior Class |
| <= 0.000015 % | <= 0.000015 % | 1st Class | |
| Environmental Stress Crack Resistance | >= 500 hour | >= 500 hour | |
| Melt Flow | 0.30 - 0.65 g/10 min @Load 5.00 kg |
0.30 - 0.65 g/10 min @Load 11.0 lb |
±10% Superior Class, ±15% 1st Class |
| Ash | <= 0.050 % | <= 0.050 % | Superior Class |
| <= 0.075 % | <= 0.075 % | 1st Class |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | >= 22.6 MPa | >= 3280 psi | |
| Elongation at Break | >= 700 % | >= 700 % | |
| Tear Strength Test | >= 21.6 | >= 21.6 | MPa |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 200 °C @Time >=1200 sec |
392 °F @Time >=0.333 hour |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | <= 2.4 @Frequency 1000 Hz |
<= 2.4 @Frequency 1000 Hz |
|
| Dielectric Strength | >= 35.0 kV/mm @Frequency 50.0 Hz |
>= 889 kV/in @Frequency 50.0 Hz |
Sample of 1 mm thickness, Alternating current |
| Dissipation Factor | <= 0.00020 @Frequency 1000 Hz |
<= 0.00020 @Frequency 1000 Hz |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Amount of impurities [pcs] | 10 | Superior Class |
| 20 | 1st Class |
Users viewing this material also viewed the following:
- Polyplastic Armlen® PP MF 40-4M Polypropylene Copolymer, 40% Calcium Carbonate
- SABIC Innovative Plastics Cycoloy® C7240P PC+ABS (Asia Pacific)
- Northstar Polymers MGP-D50A High Performance Polyurethane Cast Elastomer System 50D
- Micropol Microlink XL28/FR Black Crosslinkable Polyethylene
- Eagle Brass 101 OFE COPPER (Certified), 1/2 Hard
- Bond Laminates TEPEX® dynalite 208-C200(x)/45% Carbon - TPU Consolidated Composite Laminate
- Arkema Group Orgalloy® RS 6635 A Nylon 66 Alloy, 35% Glass Fiber (Conditioned)
- Braskem TN2005 EVA General Film Copolymer
- Beijing Chemical Industry KAIFA® 301-G15F PBT Resin
Copyright © lookpolymers.com All Rights Reserved