SABIC Innovative Plastics LNP Thermocomp WX01910L PBT

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP THERMOCOMP
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP Thermocomp WX01910L PBT.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Thermocomp* WX01910L is a compound based on Thermoplastic Polyester containing Proprietary Fillers. Characteristics of this grade are: Low Extractable.This data was supplied by SABIC-IP for the Americas region.
Physical Properties Metric English Comments
Density 1.54 g/cc
0.0556 lb/in³
ASTM D 792
Moisture Absorption at Equilibrium 0.050 %
0.050 %
23°C / 50% RH; ISO 62
0.050 %

@Time 86400 sec
 0.050 %

@Time 24.0 hour
 50% RH; ASTM D 570
Linear Mold Shrinkage, Flow 0.0040 - 0.0070 cm/cm

@Time 86400 sec
 0.0040 - 0.0070 in/in

@Time 24.0 hour
 ASTM D 955
Linear Mold Shrinkage, Transverse 0.010 - 0.040 cm/cm

@Time 86400 sec
 0.010 - 0.040 in/in

@Time 24.0 hour
 ASTM D 955
Mechanical Properties Metric English Comments
Tensile Strength at Break 102 MPa
14800 psi
5 mm/min; ISO 527
109 MPa
15800 psi
Type I, 5 mm/min; ASTM D 638
Tensile Strength, Yield 110 MPa
16000 psi
5 mm/min; ISO 527
Elongation at Break 1.9 %
1.9 %
Type I, 5 mm/min; ASTM D 638
2.0 %
2.0 %
5 mm/min; ISO 527
Tensile Modulus 9.84 GPa
1430 ksi
1 mm/min; ISO 527
10.22 GPa
1482 ksi
50 mm/min; ASTM D 638
Flexural Strength 163 MPa
23600 psi
ISO 178
164 MPa
23800 psi
1.3 mm/min, 50 mm span; ASTM D 790
Flexural Yield Strength 166 MPa
24100 psi
1.3 mm/min, 50 mm span; ASTM D 790
Flexural Modulus 8.72 GPa
1260 ksi
2 mm/min; ISO 178
8.98 GPa
1300 ksi
1.3 mm/min, 50 mm span; ASTM D 790
Izod Impact, Notched 0.640 J/cm

@Temperature 23.0 °C
 1.20 ft-lb/in

@Temperature 73.4 °F
 ASTM D 256
Izod Impact, Unnotched 5.79 J/cm

@Temperature 23.0 °C
 10.8 ft-lb/in

@Temperature 73.4 °F
 ASTM D 4812
Izod Impact, Notched (ISO) 6.00 kJ/m²

@Temperature 23.0 °C
 2.86 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 37.0 kJ/m²

@Temperature 23.0 °C
 17.6 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1U
Impact Test 2.00 J
1.48 ft-lb
Multiaxial Impact; ISO 6603
7.00 J

@Temperature 23.0 °C
 5.16 ft-lb

@Temperature 73.4 °F
 Instrumented Impact Total Energy; ASTM D 3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 36.9 µm/m-°C

@Temperature -30.0 - 30.0 °C
 20.5 µin/in-°F

@Temperature -22.0 - 86.0 °F
 ASTM D 696
CTE, linear, Transverse to Flow 115 µm/m-°C

@Temperature -30.0 - 30.0 °C
 63.9 µin/in-°F

@Temperature -22.0 - 86.0 °F
 ASTM D 696
Deflection Temperature at 0.46 MPa (66 psi) 219 °C
426 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
221 °C

@Thickness 3.20 mm
 430 °F

@Thickness 0.126 in
 unannealed; ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 197 °C
387 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
206 °C

@Thickness 3.20 mm
 403 °F

@Thickness 0.126 in
 unannealed; ASTM D 648